NORYL™ Resin N850
SABIC's Specialties Business NORYL™ N850 resin is a non-reinforced blend of polyphenylene ether (PPE) + polystyrene (PS). This high flow, injection moldable grade contains non-brominated, non-chlorinated flame retardant and carries a UL94 flame rating of 5VA at 3mm and V0 at 1.5mm along with UL746C Outdoor Suitability rating of F2. NORYL™ N850 resin exhibits high impact strength, dimensional stability, hydrolytic stability, and very low moisture absorption. This material is an excellent candidate for electrical and business equipment applications.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Electronics
- Displays
- Connectors
- Switches & Relays
Product Families
- Blends & Alloys
Other characteristics
- Brand
- NORYL™ Resin
- Density
- 1130.0 - 1130.0 kg/m³
- Polymer Name
- PPO/PS Alloy
- Flexural Modulus
- 2600.0 - 2600.0 MPa
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Consumer Goods
- Electrical & Electronics
- Flame Rating
- UL 94 5VA
- UL 94 HB
- UL 94 V0
- Technology
- Plastics
- Labeling Claims
- Bromine-free
- Chlorine-free
- Additives Included
- Flame Retardant
- Material Features
- Amorphous
- Dimensional Stability
- Flame Retardant
- High Flow
- High Flowability
- High Hydrolytic Stability
- Low Moisture Absorption
- Low Shrinkage
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Cell Phones
- Computer Components
- Connectors
- Displays
- Electrical Components
- Electrical/Electronic Applications
- Electronic Components
- Tablets
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 62 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 48 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ | 3.6 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 18 | % | ASTM D638 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 2620 | MPa | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 96 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2410 | MPa | ASTM D790 |
| Tensile Stress (Yield, 50 mm/min) ¹¹ | 66 | MPa | ISO 527 |
| Tensile Stress (Break, 50 mm/min) ¹¹ | 61 | MPa | ISO 527 |
| Tensile Strain (Yield, 50 mm/min) ¹¹ | 3.2 | % | ISO 527 |
| Tensile Strain (Break, 50 mm/min) ¹¹ | 4.5 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 2950 | MPa | ISO 527 |
Table 2 of 7
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.13 | — | ASTM D792 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.5 - 0.7 | % | SABIC method |
| Melt Flow Rate (at 220°C, 2.16 kgf) ¹¹ | 14 | g/10 min | ASTM D1238 |
| Melt Flow Rate (at 260°C, 3.8 kgf) ¹¹ | 18 | g/10 min | ASTM D1238 |
Table 3 of 7
13 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat Softening Temperature (Rate B/50) ¹¹ | 101 | °C | ASTM D1525 |
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 93 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 82 | °C | ASTM D648 |
| Heat Deflection Temperature (at 0.45 MPa, 6.4 mm, Unannealed) ¹¹ | 98 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 86 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.0000774 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000081 | 1/°C | ASTM E831 |
| Vicat Softening Temperature (Rate B/120) ¹¹ | 108 | °C | ISO 306 |
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 95 | °C | ISO 75/Bf |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 82 | °C | ISO 75/Af |
| Relative Temperature Index (Electrical) ¹¹ | 50 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ¹¹ | 50 | °C | UL 746B |
Table 4 of 7
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Hot Wire Ignition (PLC) ¹¹ | 2 | PLC Code | UL 746A |
| High Voltage Arc Track Rate (PLC) ¹¹ | 4 | PLC Code | UL 746A |
| High Ampere Arc Ignition (Surface, PLC) ¹¹ | 2 | PLC Code | UL 746A |
| Comparative Tracking Index (UL, PLC) ¹¹ | 2 | PLC Code | UL 746A |
Table 5 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 213 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 31 | J | ASTM D3763 |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 10 | kJ/m² | ISO 180/1A |
Table 6 of 7
15 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 75 - 80 | °C |
| Drying Time ⁷ | 3 - 4 | Hrs |
| Drying Time (Cumulative) ⁷ | 8 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Maximum Moisture Content ⁷ | -0.02 | % |
| Melt Temperature ⁷ | 250 - 275 | °C |
| Nozzle Temperature ⁷ | 250 - 275 | °C |
| Front - Zone 3 Temperature ⁷ | 240 - 275 | °C |
| Middle - Zone 2 Temperature ⁷ | 225 - 270 | °C |
| Rear - Zone 1 Temperature ⁷ | 215 - 265 | °C |
| Mold Temperature ⁷ | 55 - 75 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
Table 7 of 7
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Oxygen Index (LOI) | 36.4 | % | ASTM D2863 |
| Oxygen Index (LOI) | 364 | % | ASTM D2863 |
| UL Recognized (94HB Flame Class Rating) | 0.99 | mm | UL 94 |
| UL Recognized (94HB Flame Class Rating) | 1 | mm | UL 94 |
| UL Recognized (94V-0 Flame Class Rating) | 1.5 | mm | UL 94 |
| UL Recognized (94V-0 Flame Class Rating) | 1.49 | mm | UL 94 |
| UL Recognized (94-5VA Flame Class Rating) | 3 | mm | UL 94 |
| UL Recognized (94-5VA Flame Class Rating) | 2.99 | mm | UL 94 |
| UV-light (Water exposure/immersion) | F2 | — | UL 746C |