NORYL™ Resin PKN4752F
SABIC's Specialties Business NORYL PKN4752F resin is a non-reinforced, translucent, high heat blend of polyphenylene ether (PPE) + polystyrene (PS). This extrudable and injection moldable grade is FDA food contact compliant and exhibits high heat resistance, dimensional stability, and appears translucent with a yellow tint in the natural color. NORYL PKN4752F resin is an excellent candidate for high performance packaging in food, electronics, and healthcare. *See NORYL PKN4752 resin for NON FDA compliant version. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Industrial Automation
- Food & Beverage Packaging
- Industrial & Transport Packaging
- Non-Food Consumer Packaging
Product Families
- Blends & Alloys
Other characteristics
- Brand
- NORYL™ Resin
- Density
- 1080.0 - 1080.0 kg/m³
- Polymer Name
- PPO/PS Alloy
- Processing Methods
- Extrusion
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.. ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Color
- Translucent
- Transparent
- Markets
- Electrical & Electronics
- Printing & Packaging
- Technology
- Plastics
- Labeling Claims
- Food Contact Acceptable
- No Added PFAS
- Material Features
- Amorphous
- Dimensional Stability
- Food Contact Acceptable
- High Hydrolytic Stability
- High Temperature Resistance
- Low Moisture Absorption
- Low Shrinkage
- Low Specific Gravity
- Country Availability
- Canada
- Mexico
- USA
- Plastics and Elastomers End Uses
- Consumer Applications
- Electrical/Electronic Applications
- Flexible Packaging
- Food Packaging
- Industrial Applications
- Thin Walled Packaging
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
Technical data
Table 1 of 5
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 86 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 73 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ | 6 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 15 | % | ASTM D638 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 3000 | MPa | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 144 | MPa | ASTM D790 |
| Flexural Stress (Yield, 2.6 mm/min, 100 mm span) ¹¹ | 136 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 3150 | MPa | ASTM D790 |
| Flexural Modulus (at 2.6 mm/min, 100 mm span) ¹¹ | 2940 | MPa | ASTM D790 |
Table 2 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.08 | — | ASTM D792 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.6 - 0.9 | % | SABIC method |
Table 3 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat Softening Temperature (Rate B/50) ¹¹ | 173 | °C | ASTM D1525 |
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 160 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 151 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 151 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000063 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.0000558 | 1/°C | ASTM E831 |
Table 4 of 5
14 rows| Characteristic | Value | Unit |
|---|---|---|
| Adapter Temperature | 240 - 265 | °C |
| Barrel - Zone 1 Temperature | 205 - 225 | °C |
| Barrel - Zone 2 Temperature | 215 - 240 | °C |
| Barrel - Zone 3 Temperature | 240 - 265 | °C |
| Barrel - Zone 4 Temperature | 240 - 265 | °C |
| Die Temperature | 240 - 265 | °C |
| Drying Temperature | 70 - 80 | °C |
| Drying Time | 2 - 4 | Hrs |
| Drying Time (Cumulative) | 8 | Hrs |
| Maximum Moisture Content | 0 | % |
| Melt Temperature | 265 - 275 | °C |
| Roll Stack Temperature - Bottom | 105 - 120 | °C |
Table 5 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 32 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 6 | J | ASTM D3763 |