NORYL™ Resin SE1GFN1
SABIC's Specialties Business NORYL™ SE1GFN1 resin is a 10% glass fiber reinforced blend of polyphenylene ether (PPE) + polystyrene (PS). This injection moldable grade contains non-brominated, non-chlorinated flame retardant and carries a UL94 flame rating of V1 at 1.5mm along with UL746C Outdoor Suitability rating of F1 and RTI 110C. NORYL™ SE1GFN1 exhibits high heat resistance, good dielectric strength, dimensional stability, hydrolytic stability, and very low moisture absorption. This material is an excellent candidate for appliance internals, indoor and outdoor electrical enclosures / housings / connectors.
Product families
- Blends & Alloys
Other characteristics
- Brand
- NORYL™ Resin
- Density
- 1160.0 - 1160.0 kg/m³
- Polymer Name
- PPO/PS Alloy
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Healthcare & Pharma
- Industrial
- Flame Rating
- UL 94 5VA
- UL 94 V1
- Technology
- Plastics
- Labeling Claims
- Bromine-free
- Chlorine-free
- Fillers Included
- Glass Fiber
- Additives Included
- Flame Retardant
- Heat Stabilizer
- Material Features
- Amorphous
- Dimensional Stability
- Flame Retardant
- Good Stiffness
- Heat Stabilized
- High Hydrolytic Stability
- High Stiffness
- Low Moisture Absorption
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Certifications and Compliance
- UL 94
Technical data
Table 1 of 7
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Taber Abrasion (CS-17, 1 kg) ¹¹ | 50 | mg/1000cy | SABIC method |
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 74 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 5 | % | ASTM D638 |
| Tensile Stress (Yield, 5 mm/min) ¹¹ | 75 | MPa | ISO 527 |
| Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹ | 119 | MPa | ASTM D790 |
| Tensile Stress (Break, 5 mm/min) ¹¹ | 70 | MPa | ISO 527 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 3990 | MPa | ASTM D790 |
| Tensile Strain (Yield, 5 mm/min) ¹¹ | 2.5 | % | ISO 527 |
| Hardness (Rockwell L) ¹¹ | 104 | — | ASTM D785 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 3 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 4000 | MPa | ISO 527 |
| Flexural Stress (Yield, at 2 mm/min) ¹¹ | 110 | MPa | ISO 178 |
Table 2 of 7
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.16 | — | ASTM D792 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.07 | % | ASTM D570 |
| Water Absorption (at 23°C, saturated) ¹¹ | 0.22 | % | ISO 62-1 |
| Water Absorption (at 23°C, saturated) ¹¹ | 0.22 | % | ASTM D570 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.3 - 0.5 | % | SABIC method |
| Mold Shrinkage (on Tensile Bar, flow) ᵍ ¹¹ | 0.3 - 0.5 | % | SABIC method |
| Density ¹¹ | 1.17 | g/cm³ | ISO 1183 |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.07 | % | ISO 62 |
| Melt Volume Rate (at 280°C, 10.0 kg) ¹¹ | 15 | cm³/10 min | ISO 1133 |
Table 3 of 7
20 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat Softening Temperature (Rate B/50) ¹¹ | 140 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 147 | °C | ASTM D1525 |
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 131 | °C | ASTM D648 |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 110 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 105 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 110 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 1.10E+02 | °C | UL 746B |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000055 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000055 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000068 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000068 | 1/°C | ISO 11359-2 |
| Thermal Conductivity ¹¹ | 0.27 | W/m-°C | ISO 8302 |
Table 4 of 7
25 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volume Resistivity ¹¹ | 1.00E+15 | Ω.cm | IEC 60093 |
| Volume Resistivity ¹¹ | 1.00E+15 | Ω.cm | ASTM D257 |
| Relative Permittivity (50/60 Hz) ¹¹ | 2.8 | — | IEC 60250 |
| Relative Permittivity (50/60 Hz) ¹¹ | 3 | — | ASTM D150 |
| Relative Permittivity (1 MHz) ¹¹ | 2.7 | — | IEC 60250 |
| Relative Permittivity (1 MHz) ¹¹ | 3 | — | ASTM D150 |
| Dissipation Factor (at 50/60 Hz) ¹¹ | 0.0017 | — | ASTM D150 |
| Dissipation Factor (at 50/60 Hz) ¹¹ | 0.005 | — | IEC 60250 |
| Dissipation Factor (at at 1 MHz) ¹¹ | 0.003 | — | IEC 60250 |
| Dissipation Factor (at at 1 MHz) ¹¹ | 0.0016 | — | ASTM D150 |
| High Voltage Arc Track Rate (PLC) ¹¹ | 4 | PLC Code | UL 746A |
| Comparative Tracking Index (UL, PLC) ¹¹ | 2 | PLC Code | UL 746A |
Table 5 of 7
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 96 | J/m | ASTM D256 |
| Izod Impact (Notched, at -40°C) ¹¹ | 69 | J/m | ASTM D256 |
| Izod Impact (Notched, 80*10*3, at -40°C) ¹¹ | 6 | kJ/m² | ISO 180/1A |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 25 | kJ/m² | ISO 180/1U |
| Izod Impact (Unnotched, 80*10*4, at -30°C) ¹¹ | 25 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 7 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at -30°C) ¹¹ | 6 | kJ/m² | ISO 180/1A |
| Charpy Impact (at 23°C, V-notch Edgew 80*10*3 sp=62mm) ¹¹ | 6 | kJ/m² | ISO 179/1eA |
| Charpy Impact (at -30°C, V-notch Edgew 80*10*3 sp=62mm) ¹¹ | 5 | kJ/m² | ISO 179/1eA |
| Charpy Impact (at -40°C, V-notch Edgew 80*10*3 sp=62mm) ¹¹ | 5 | kJ/m² | ISO 179/1eA |
| Charpy Impact (at -30°C, Unnotch Edgew 80*10*3 sp=62mm) ¹¹ | 30 | kJ/m² | ISO 179/1eU |
| Charpy Impact (at 23°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹ | 30 | kJ/m² | ISO 179/1eU |
Table 6 of 7
22 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 105 - 110 | °C |
| Drying Temperature ⁷ | 100 - 120 | °C |
| Drying Time ⁷ | 3 - 4 | Hrs |
| Drying Time ⁷ | 2 - 3 | Hrs |
| Drying Time (Cumulative) ⁷ | 8 | Hrs |
| Melt Temperature ⁷ | 280 - 310 | °C |
| Melt Temperature ⁷ | 280 - 300 | °C |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Nozzle Temperature ⁷ | 280 - 310 | °C |
| Nozzle Temperature ⁷ | 260 - 280 | °C |
| Front - Zone 3 Temperature ⁷ | 280 - 300 | °C |
| Front - Zone 3 Temperature ⁷ | 270 - 310 | °C |
Table 7 of 7
19 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94-5VA Flame Class Rating) ʳ | min. 2.5 | mm | UL 94 |
| UL Recognized (94V-1 Flame Class Rating) ʳ | min. 0.8 | mm | UL 94 |
| UL Recognized (94V-1 Flame Class Rating) ʳ | min. 1.5 | mm | UL 94 |
| UL Recognized (94V-1 Flame Class Rating) ʳ | min. 0.44 | mm | UL 94 |
| Oxygen Index (LOI) ʳ | 30 | % | ISO 4589 |
| Oxygen Index (LOI) ʳ | 33.9 | % | ASTM D2863 |
| UV-light (Water exposure/immersion) ʳ | F1 | — | UL 746C |
| UV-light (Water exposure/immersion) ʳ | F2 | — | UL 746C |
| Glow Wire Flammability Index (at 1 mm) ʳ | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index (at 1.5 mm) ʳ | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index (at 2 mm) ʳ | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index (at 2.5 mm) ʳ | 960 | °C | IEC 60695-2-12 |