NORYL™ Resin HS2000X
SABIC's Specialties Business NORYL™ HS2000X resin is a 17% mineral reinforced blend of polyphenylene ether (PPE) + polystyrene (PS). This injection moldable grade contains non-brominated, non-chlorinated flame retardant and carries a UL94 flame rating of 5VA at 2mm and V0 at 1.5m along with UL746C Outdoor Suitability rating of F1. NORYL™ HS2000X resin exhibits strong electrical performance, dimensional stability, very low moisture absorption, and hydrolytic stability. This material is an excellent candidate for electronic / electrical indoor and outdoor applications including air conditioner parts, smoke detector covers, pool + spa pump parts and housings.
Product families
- Blends & Alloys
Other characteristics
- Brand
- NORYL™ Resin
- Density
- 1250.0 - 1250.0 kg/m³
- Polymer Name
- PPO/PS Alloy
- Flexural Modulus
- 3800.0 - 3800.0 MPa
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Healthcare & Pharma
- Industrial
- Flame Rating
- UL 94 5VA
- UL 94 V0
- Technology
- Plastics
- Labeling Claims
- Bromine-free
- Chlorine-free
- Fillers Included
- Mineral
- Additives Included
- Flame Retardant
- Heat Stabilizer
- Impact Modifier
- Mold Release Agent
- Material Features
- Amorphous
- Dimensional Stability
- Flame Retardant
- Good Mold Release
- Good Stiffness
- Heat Stabilized
- High Hydrolytic Stability
- High Stiffness
- Country Availability
- Canada
- Mexico
- USA
- Certifications and Compliance
- UL 94
Technical data
Table 1 of 7
16 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 5 mm/min) ¹¹ | 74 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 60 | MPa | ASTM D638 |
| Tensile Strain (Yield) ¹¹ | 3.8 | % | ASTM D638 |
| Tensile Strain (Yield) ¹¹ | 3.7 | % | ISO 527 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 8.4 | % | ASTM D638 |
| Tensile Modulus (at 5 mm/min) ¹¹ | 3650 | MPa | ASTM D638 |
| Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹ | 117 | MPa | ASTM D790 |
| Flexural Stress (Yield, 2.6 mm/min, 100 mm span) ¹¹ | 117 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 3670 | MPa | ASTM D790 |
| Flexural Modulus (at 2.6 mm/min, 100 mm span) ¹¹ | 3550 | MPa | ASTM D790 |
| Tensile Stress (Yield) ¹¹ | 71 | MPa | ISO 527 |
| Tensile Stress (Break) ¹¹ | 57 | MPa | ISO 527 |
Table 2 of 7
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.25 | — | ASTM D792 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.5 - 0.7 | % | SABIC method |
| Melt Flow Rate (at 280°C, 5.0 kgf) ¹¹ | 7.6 | g/10 min | ASTM D1238 |
| Melt Flow Rate (at 300°C, 5.0 kgf) ¹¹ | 7.6 | g/10 min | ASTM D1238 |
| Melt Volume Rate (at 280°C, 5.0 kg) ¹¹ | 6 | cm³/10 min | ISO 1133 |
| Melt Volume Rate (at 300°C, 5.0 kg) ¹¹ | 6 | cm³/10 min | ISO 1133 |
Table 3 of 7
13 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 117 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 108 | °C | ASTM D648 |
| Heat Deflection Temperature (at 0.45 MPa, 6.4 mm, Unannealed) ¹¹ | 128 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 116 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.0000706 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.0000776 | 1/°C | ASTM E831 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 132 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/120) ¹¹ | 136 | °C | ISO 306 |
| Heat Deflection Temperature/Be (at 0.45MPa, Edgew 120*10*4, sp=100mm) ¹¹ | 126 | °C | ISO 75/Be |
| Heat Deflection Temperature/Ae (at 1.8 Mpa, Edgew 120*10*4, sp=100mm) ¹¹ | 111 | °C | ISO 75/Ae |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 100 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 85 | °C | UL 746B |
Table 4 of 7
13 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volume Resistivity ¹¹ | 1.20E+16 | Ω.cm | ASTM D257 |
| Surface Resistivity ¹¹ | min. 1.E+16 | Ω | ASTM D257 |
| Dielectric Strength (in oil, at 3.2mm) ¹¹ | 17.3 | kV/mm | ASTM D149 |
| Relative Permittivity (50/60 Hz) ¹¹ | 2.89 | — | ASTM D150 |
| Relative Permittivity (1 MHz) ¹¹ | 2.7 | — | ASTM D150 |
| Dissipation Factor (at 50/60 Hz) ¹¹ | 0.017 | — | ASTM D150 |
| Dissipation Factor (at at 1 MHz) ¹¹ | 0.0044 | — | ASTM D150 |
| High Voltage Arc Track Rate (PLC) ¹¹ | 3 | PLC Code | UL 746A |
| Comparative Tracking Index (UL, PLC) ¹¹ | 2 | PLC Code | UL 746A |
| High Ampere Arc Ignition (PLC 2) ¹¹ | min. 3 | mm | UL 746A |
| High Ampere Arc Ignition (PLC 3) ¹¹ | min. 1.5 | mm | UL 746A |
| Hot Wire Ignition (PLC 0) ¹¹ | min. 1.5 | mm | UL 746A |
Table 5 of 7
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, at 23°C) ¹¹ | 2230 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 131 | J/m | ASTM D256 |
| Izod Impact (Reverse Notched, 3.2 mm) ¹¹ | 811 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 443 | J | ASTM D3763 |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 9 | kJ/m² | ISO 180/1A |
| Charpy Impact (Notched, at 23°C) ¹¹ | 10 | kJ/m² | ISO 179/2C |
Table 6 of 7
13 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 105 - 110 | °C |
| Drying Time ⁷ | 3 - 4 | Hrs |
| Drying Time (Cumulative) ⁷ | 8 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 280 - 310 | °C |
| Nozzle Temperature ⁷ | 280 - 310 | °C |
| Front - Zone 3 Temperature ⁷ | 270 - 310 | °C |
| Middle - Zone 2 Temperature ⁷ | 260 - 305 | °C |
| Rear - Zone 1 Temperature ⁷ | 250 - 300 | °C |
| Mold Temperature ⁷ | 75 - 105 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed ⁷ | 20 - 100 | rpm |
Table 7 of 7
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94-5VA Flame Class Rating) ʳ | min. 2 | mm | UL 94 |
| UL Recognized (94V-0 Flame Class Rating) ʳ | min. 1.5 | mm | UL 94 |
| Glow Wire Flammability Index (at 1 mm) ʳ | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index (at 2 mm) ʳ | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index (at 3 mm) ʳ | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignitability Temperature (at 1.0 mm) ʳ | 850 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature (at 2.0 mm) ʳ | 800 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature (at 3.0 mm) ʳ | 800 | °C | IEC 60695-2-13 |
| UV-light (Water exposure/immersion) ʳ | F1 | — | UL 746C |