NORYL™ Resin PX2935
SABIC's Specialties Business NORYL PX2935 resin is a 20% glass fiber reinforced blend of polyphenylene ether (PPE) + polystyrene (PS). This high impact extrusion grade exhibits high impact strength, dimensional stability, hydrolytic stability, and very low moisture absorption. This material is an excellent candidate for industrial applications. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Industrial Automation
Product Families
- Blends & Alloys
Other characteristics
- Brand
- NORYL™ Resin
- Density
- 1200.0 - 1200.0 kg/m³
- Polymer Name
- PPO/PS Alloy
- Flexural Modulus
- 5590.0 - 5590.0 MPa
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.. ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Fillers Included
- Glass Fiber
- Material Features
- Amorphous
- Dimensional Stability
- Excellent Stiffness
- Good Stiffness
- High Hydrolytic Stability
- High Stiffness
- High Strength
- Low Moisture Absorption
- Country Availability
- China (Mainland)
- Plastics and Elastomers End Uses
- Industrial Applications
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 4
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield) ¹¹ | 82 | MPa | SABIC - Japan Method |
| Tensile Strain (Break) ¹¹ | 4 - 6 | % | SABIC - Japan Method |
| Flexural Stress ¹¹ | 133 | MPa | ASTM D790 |
| Flexural Modulus ¹¹ | 5590 | MPa | ASTM D790 |
Table 2 of 4
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.2 | — | ASTM D792 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.06 | % | ASTM D570 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.2 - 0.4 | % | SABIC method |
| Melt Flow Rate (at 300°C, 5.0 kgf) ¹¹ | 29.3 | g/10 min | ASTM D1238 |
Table 3 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 125 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -30°C to 30°C) ¹¹ | 0.000022 - 0.000071 | 1/°C | TMA |
Table 4 of 4
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 99 | J/m | ASTM D256 |