NORYL™ Resin PCN2910
SABIC's Specialties Business NORYL™ PCN2910 resin is a 35% glass fiber and mineral reinforced blend of polyphenylene ether (PPE) + polystyrene (PS). This high modulus, injection moldable grade contains non-brominated, non-chlorinated flame retardant and carries a UL94 flame rating of 5VB at 2.3mm, V0 at 3mm, and V1 at 1.5mm. NORYL™ PCN2910 resin exhibits good dimensional stability, low specific gravity, and Low Warpage. It is an excellent candidate for printer chassis applications where high modulus and tight tolerance molding are required.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Stationery
- Art & Office Supplies
- Chassis & Brake
- Glazing & Window Elements
- Interior Fixtures
- Consumer Electronics
- Displays
- Connectors
- Housings & Enclosures
- Switches & Relays
Product Families
- Blends & Alloys
Other characteristics
- Brand
- NORYL™ Resin
- Density
- 1380.0 - 1380.0 kg/m³
- Polymer Name
- PPO/PS Alloy
- Flexural Modulus
- 9130.0 - 9130.0 MPa
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Flame Rating
- UL 94 5VB
- UL 94 V0
- UL 94 V1
- Technology
- Plastics
- Labeling Claims
- Bromine-free
- Chlorine-free
- Fillers Included
- Glass Fiber
- Glass/Mica
- Glass/Mineral
- Mineral
- Additives Included
- Flame Retardant
- Mold Release Agent
- Material Features
- Amorphous
- Dimensional Stability
- Flame Retardant
- Good Mold Release
- Good Stiffness
- High Hydrolytic Stability
- High Stiffness
- High Strength
- Country Availability
- China (Mainland)
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Building Materials
- Cash Dispenser (ATM)
- Cell Phones
- Chassis
- Circuit Protection
- Computer Components
- Construction Applications
- Covers
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 5 mm/min) ¹¹ | 123 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 10 mm/min) ¹¹ | 115 | MPa | SABIC - Japan Method |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 1.5 | % | ASTM D638 |
| Tensile Strain (Yield, Type I, 10 mm/min) ¹¹ | 5 | % | SABIC - Japan Method |
| Tensile Modulus (at 5 mm/min) ¹¹ | 11370 | MPa | ASTM D638 |
| Flexural Stress (Yield, 2.6 mm/min, 100 mm span) ¹¹ | 159 | MPa | ASTM D790 |
| Flexural Modulus (at 2.6 mm/min, 100 mm span) ¹¹ | 8940 | MPa | ASTM D790 |
| Tensile Stress (Yield, 5 mm/min) ¹¹ | 106 | MPa | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 1.3 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 10600 | MPa | ISO 527 |
| Flexural Stress (Yield, at 2 mm/min) ¹¹ | 160 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 9130 | MPa | ISO 178 |
Table 2 of 6
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.38 | — | ASTM D792 |
| Mold Shrinkage (flow) ᵍ ¹¹ | 0.25 - 0.3 | % | SABIC method |
| Melt Flow Rate (at 300°C, 2.16 kgf) ¹¹ | 11 | g/10 min | ASTM D1238 |
Table 3 of 6
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat Softening Temperature (Rate B/50) ¹¹ | 140 | °C | ASTM D1525 |
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 125 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -30°C to 30°C) ¹¹ | 0.000021 - 0.000033 | 1/°C | TMA |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 129 | °C | ISO 75/Af |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 65 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 65 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 65 | °C | UL 746B |
Table 4 of 6
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, at 23°C) ¹¹ | 331 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 68 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 7 | J | ASTM D3763 |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 14 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 5 | kJ/m² | ISO 180/1A |
| Charpy Impact (Notched, at 23°C) ¹¹ | 4 | kJ/m² | ISO 179/2C |
| Charpy Impact (at 23°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹ | 20 | kJ/m² | ISO 179/1eU |
Table 5 of 6
13 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 105 - 110 | °C |
| Drying Time ⁷ | 3 - 4 | Hrs |
| Drying Time (Cumulative) ⁷ | 8 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 295 - 315 | °C |
| Nozzle Temperature ⁷ | 295 - 315 | °C |
| Front - Zone 3 Temperature ⁷ | 280 - 315 | °C |
| Middle - Zone 2 Temperature ⁷ | 270 - 310 | °C |
| Rear - Zone 1 Temperature ⁷ | 260 - 305 | °C |
| Mold Temperature ⁷ | 75 - 105 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed ⁷ | 20 - 100 | rpm |
Table 6 of 6
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94-5VB Flame Class Rating) ʳ | min. 2.3 | mm | UL 94 |
| UL Recognized (94V-0 Flame Class Rating) ʳ | min. 3 | mm | UL 94 |
| UL Recognized (94V-1 Flame Class Rating) ʳ | min. 1.5 | mm | UL 94 |