NORYL™ Resin NH4030B
SABIC's Specialties Business NORYL NH4030B resin is a non-reinforced blend of polyphenylene ether (PPE) + polystyrene (PS). This high flow, injection moldable and extrusion grade contains non-brominated, non-chlorinated flame retardant and carries a UL94 flame rating of V0 at 1.5mm along with lower smoke production upon burning and low specific gravity for light-weight parts. NORYL NH4030B resin may be an excellent candidate for rail interior, electrical conduit, cable management, and ceiling-mounted electric applications. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Exterior & Body
- Interior
- Glazing & Window Elements
- Interior Fixtures
- Consumer Electronics
- Displays
- Circuit Breakers
- Conduits & Cable Management
- Connectors
- Switches & Relays
- Rail & Mass Transit
Product Families
- Blends & Alloys
Other characteristics
- Brand
- NORYL™ Resin
- Density
- 1110.0 - 1110.0 kg/m³
- Polymer Name
- PPO/PS Alloy
- Flexural Modulus
- 2380.0 - 2380.0 MPa
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Flame Rating
- UL 94 V0
- Technology
- Plastics
- Labeling Claims
- Bromine-free
- Chlorine-free
- No Added PFAS
- Additives Included
- Flame Retardant
- Heat Stabilizer
- Impact Modifier
- Material Features
- Amorphous
- Dimensional Stability
- Flame Retardant
- Heat Stabilized
- High Flow
- High Flowability
- High Hydrolytic Stability
- Impact Modified
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Automotive Applications
- Building Materials
- Cell Phones
- Commercial Appliance
- Computer Components
- Conduit
- Construction Applications
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 8
15 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 56 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 46 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ | 4.2 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 27.5 | % | ASTM D638 |
| Tensile Modulus (at 5 mm/min) ¹¹ | 2450 | MPa | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 90 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2400 | MPa | ASTM D790 |
| Tensile Stress (Yield, 50 mm/min) ¹¹ | 54 | MPa | ISO 527 |
| Tensile Stress (Break, 50 mm/min) ¹¹ | 47 | MPa | ISO 527 |
| Tensile Strain (Break) ¹¹ | 2.78E+01 | % | ISO 527 |
| Tensile Strain (Yield, 50 mm/min) ¹¹ | 4 | % | ISO 527 |
| Tensile Strain (Break, 50 mm/min) ¹¹ | 27.8 | % | ISO 527 |
Table 2 of 8
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.11 | — | ASTM D792 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.5 - 0.8 | % | SABIC method |
| Melt Flow Rate (at 280°C, 5.0 kgf) ¹¹ | 18.3 | g/10 min | ASTM D1238 |
| Melt Flow Rate (at 300°C, 5.0 kgf) ¹¹ | 42.7 | g/10 min | ASTM D1238 |
| Density ¹¹ | 1.11 | g/cm³ | ISO 1183 |
| Water Absorption (at 23°C, saturated) ¹¹ | 0.27 | % | ISO 62-1 |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.04 | % | ISO 62 |
| Melt Volume Rate (at 280°C, 5.0 kg) ¹¹ | 17 | cm³/10 min | ISO 1133 |
| Melt Volume Rate (at 300°C, 5.0 kg) ¹¹ | 41 | cm³/10 min | ISO 1133 |
Table 3 of 8
13 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat Softening Temperature (Rate B/50) ¹¹ | 127 | °C | ASTM D1525 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 127 | °C | ISO 306 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 106 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 112 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.0000839 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.0000839 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.0000854 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.0000854 | 1/°C | ASTM E831 |
| Vicat Softening Temperature (Rate B/120) ¹¹ | 128 | °C | ISO 306 |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 107 | °C | ISO 75/Af |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 105 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 65 | °C | UL 746B |
Table 4 of 8
14 rows| Characteristic | Value | Unit |
|---|---|---|
| Adapter Temperature | 215 - 250 | °C |
| Barrel - Zone 1 Temperature | 215 - 250 | °C |
| Barrel - Zone 2 Temperature | 215 - 250 | °C |
| Barrel - Zone 3 Temperature | 215 - 250 | °C |
| Barrel - Zone 4 Temperature | 215 - 250 | °C |
| Die Temperature | 215 - 250 | °C |
| Drying Temperature | 95 - 105 | °C |
| Drying Time | 2 - 4 | Hrs |
| Drying Time (Cumulative) | 12 | Hrs |
| Maximum Moisture Content | 0.07 | % |
| Melt Temperature | 215 - 250 | °C |
| Roll Stack Temperature - Bottom | 90 - 150 | °C |
Table 5 of 8
14 rows| Characteristic | Value | Unit |
|---|---|---|
| Adapter Temperature | 215 - 250 | °C |
| Barrel - Zone 1 Temperature | 215 - 250 | °C |
| Barrel - Zone 2 Temperature | 215 - 250 | °C |
| Barrel - Zone 3 Temperature | 215 - 250 | °C |
| Barrel - Zone 4 Temperature | 215 - 250 | °C |
| Die Temperature | 215 - 250 | °C |
| Drying Temperature | 95 - 105 | °C |
| Drying Time | 2 - 4 | Hrs |
| Drying Time (Cumulative) | 12 | Hrs |
| Maximum Moisture Content | 0.07 | % |
| Melt Temperature | 215 - 250 | °C |
| Calibrator Temperature | 30 - 60 | °C |
Table 6 of 8
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 200 | J/m | ASTM D256 |
| Izod Impact (Notched, at -30°C) ¹¹ | 117 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 46 | J | ASTM D3763 |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 15 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at -30°C) ¹¹ | 11 | kJ/m² | ISO 180/1A |
| Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 19 | kJ/m² | ISO 179/1eA |
Table 7 of 8
14 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 95 - 105 | °C |
| Drying Time ⁷ | 2 - 4 | Hrs |
| Drying Time (Cumulative) ⁷ | 12 | Hrs |
| Maximum Moisture Content ⁷ | 0.07 | % |
| Melt Temperature ⁷ | 260 - 290 | °C |
| Nozzle Temperature ⁷ | 260 - 290 | °C |
| Front - Zone 3 Temperature ⁷ | 250 - 290 | °C |
| Middle - Zone 2 Temperature ⁷ | 240 - 280 | °C |
| Rear - Zone 1 Temperature ⁷ | 225 - 275 | °C |
| Mold Temperature ⁷ | 65 - 100 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed ⁷ | 20 - 100 | rpm |
Table 8 of 8
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94V-0 Flame Class Rating) ʳ | min. 1.5 | mm | UL 94 |
| Flame Spread Index (at 1.52mm) ʳ | 15 | — | ASTM E162 |
| Vertical Burn A (at 60s, 1.52mm, passes) ʳ | 0 | Seconds | FAR 25.853 |
| Vertical Burn B (at 12s, 1.52mm, passes) ʳ | 4 | Seconds | FAR 25.853 |
| NBS Smoke Density (Flaming, 4 min, 1.52mm) ʳ | 29 | — | ASTM E662 |
| NBS Smoke Density (Flaming, 4 min, 3.2mm) ʳ | 35 | — | ASTM E662 |
| NBS Smoke Density (Flaming, 20 min, 3.2mm) ʳ | 126 | — | ASTM E662 |
| Draeger Tube Toxicity, Non-Flaming (at 1.52mm) ʳ | Pass | — | AITM 3.0005, ABD0031 |
| NBS Smoke Density (Non-Flaming, 4 min, 1.52mm) ʳ | 7 | — | ASTM E662 |
| Draeger Tube Toxicity, Flaming (at 1.52mm) ʳ | Pass | — | AITM 3.0005, ABD0031 |