NORYL™ Resin FP5140HF
SABIC's Specialties Business NORYL™ FP5140HF resin is an impact modified, unreinforced blend of polyphenylene ether (PPE) + polystyrene (PS). This injection moldable grade contains non-brominated, non-chlorinated flame retardant with a UL94 flame rating of V1 at 1.5mm. NORYL™ FP5140HF resin was designed to have very good dimensional stability with high flow and exhibits good rheological properties, high heat resistance, hydrolysis resistance, and very low density. The combination of these properties makes this material an excellent candidate for Flat Panel TV enclosure applications.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Electronics
- Displays
Product Families
- Blends & Alloys
Other characteristics
- Brand
- NORYL™ Resin
- Density
- 1110.0 - 1110.0 kg/m³
- Polymer Name
- PPO/PS Alloy
- Flexural Modulus
- 2450.0 - 2450.0 MPa
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Consumer Goods
- Electrical & Electronics
- Flame Rating
- UL 94 V1
- Technology
- Plastics
- Labeling Claims
- Bromine-free
- Chlorine-free
- Additives Included
- Flame Retardant
- Heat Stabilizer
- Material Features
- Amorphous
- Dimensional Stability
- Flame Retardant
- Good Processability
- Heat Stabilized
- High Flow
- High Flowability
- High Hydrolytic Stability
- Country Availability
- Canada
- Mexico
- USA
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Cell Phones
- Computer Components
- Displays
- Electrical/Electronic Applications
- Enclosure
- Tablets
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus (at 50 mm/min) ¹¹ | 2940 | MPa | ASTM D638 |
| Tensile Stress (Yield, 50 mm/min) ¹¹ | 48 | MPa | ISO 527 |
| Tensile Stress (Break, 50 mm/min) ¹¹ | 44 | MPa | ISO 527 |
| Tensile Strain (Yield, 50 mm/min) ¹¹ | 2.7 | % | ISO 527 |
| Tensile Strain (Break, 50 mm/min) ¹¹ | 21.4 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 2530 | MPa | ISO 527 |
| Flexural Stress (Yield, at 2 mm/min) ¹¹ | 80 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 2450 | MPa | ISO 178 |
Table 2 of 6
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.11 | — | ASTM D792 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.5 - 0.7 | % | SABIC method |
| Density ¹¹ | 1.11 | g/cm³ | ISO 1183 |
| Water Absorption (at 23°C, saturated) ¹¹ | 0.18 | % | ISO 62-1 |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.05 | % | ISO 62 |
| Melt Volume Rate (at 280°C, 1.2 kg) ¹¹ | 17 | cm³/10 min | ISO 1133 |
| Melt Volume Rate (at 280°C, 2.16 kg) ¹¹ | 48 | cm³/10 min | ISO 1133 |
Table 3 of 6
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat Softening Temperature (Rate B/50) ¹¹ | 97 | °C | ASTM D1525 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 97 | °C | ISO 306 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 78 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000083 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000083 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000077 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000077 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature (Rate B/120) ¹¹ | 100 | °C | ISO 306 |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 80 | °C | ISO 75/Af |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 65 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 65 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 65 | °C | UL 746B |
Table 4 of 6
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 6 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at -30°C) ¹¹ | 5 | kJ/m² | ISO 180/1A |
| Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 7 | kJ/m² | ISO 179/1eA |
Table 5 of 6
9 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 70 - 80 | °C |
| Drying Time ⁷ | 2 - 3 | Hrs |
| Melt Temperature ⁷ | 250 - 285 | °C |
| Nozzle Temperature ⁷ | 240 - 270 | °C |
| Front - Zone 3 Temperature ⁷ | 250 - 285 | °C |
| Middle - Zone 2 Temperature ⁷ | 230 - 260 | °C |
| Rear - Zone 1 Temperature ⁷ | 200 - 220 | °C |
| Hopper Temperature ⁷ | 60 - 80 | °C |
| Mold Temperature ⁷ | 40 - 65 | °C |
Table 6 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94V-1 Flame Class Rating) ʳ | min. 1.5 | mm | UL 94 |