NORYL™ Resin FE1630PW
SABIC's Specialties Business NORYL™ FE1630PW resin is a 30% glass fiber reinforced blend of polyphenylene ether (PPE) + polystyrene (PS). This injection moldable material is FC EU, FDA food contact compliant, NSF/ANSI 61*ACS, WRAS, KTW, and W270 listed for global potable water use. NORYL™ FE1630PW resin exhibits excellent long-term hydrolytic stability, very low moisture absorption, heat / hot water resistance and is an excellent candidate for a variety of water management applications such as pump housings, impellers, shower/faucet, membrane housings and valves. *NSF certification is color dependent. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Pipes & Plumbing
- Water Treatment
Product Families
- Blends & Alloys
Other characteristics
- Brand
- NORYL™ Resin
- Density
- 1300.0 - 1300.0 kg/m³
- Polymer Name
- PPO/PS Alloy
- Flexural Modulus
- 8120.0 - 8120.0 MPa
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Building & Construction
- Industrial
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Labeling Claims
- Food Contact Acceptable
- No Added PFAS
- Fillers Included
- Glass Fiber
- Additives Included
- Heat Stabilizer
- Material Features
- Amorphous
- Dimensional Stability
- Excellent Stiffness
- Food Contact Acceptable
- Good Stiffness
- Heat Stabilized
- High Hydrolytic Stability
- High Stiffness
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Certifications and Compliance
- NSF Standard 61 for Drinking Water
- UL 94
- Plastics and Elastomers End Uses
- Faucet System Components
- Filters
- Fittings
- Gears
- Hygiene
- Potable Water Applications
- Pump Parts
- Water Management
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 134 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 2.4 | % | ASTM D638 |
| Tensile Modulus (at 5 mm/min) ¹¹ | 9570 | MPa | ASTM D638 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 7760 | MPa | ASTM D790 |
| Taber Abrasion (CS-17, 1 kg) ¹¹ | 65 | mg/1000cy | SABIC method |
| Tensile Stress (Break, 5 mm/min) ¹¹ | 133 | MPa | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 2.5 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 9600 | MPa | ISO 527 |
| Flexural Stress (Break, 2 mm/min) ¹¹ | 192 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 8120 | MPa | ISO 178 |
| Ball Indentation Hardness (H358/30) ¹¹ | 240 | MPa | ISO 2039-1 |
Table 2 of 6
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.1 - 0.3 | % | SABIC method |
| Mold Shrinkage (xflow, 3.2 mm) ᵍ ¹¹ | 0.2 - 0.5 | % | SABIC method |
| Melt Flow Rate (at 300°C, 5.0 kgf) ¹¹ | 9 | g/10 min | ASTM D1238 |
| Density ¹¹ | 1.3 | g/cm³ | ISO 1183 |
| Water Absorption (at 23°C, saturated) ¹¹ | 0.2 | % | ISO 62-1 |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.06 | % | ISO 62 |
| Melt Volume Rate (at 300°C, 10.0 kg) ¹¹ | 30 | cm³/10 min | ISO 1133 |
Table 3 of 6
13 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 145 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.00003 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000025 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.00007 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.00006 | 1/°C | ASTM E831 |
| Vicat Softening Temperature (Rate A/50) ¹¹ | 165 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 154 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/120) ¹¹ | 158 | °C | ISO 306 |
| Heat Deflection Temperature/Be (at 0.45MPa, Edgew 120*10*4, sp=100mm) ¹¹ | 150 | °C | ISO 75/Be |
| Heat Deflection Temperature/Ae (at 1.8 Mpa, Edgew 120*10*4, sp=100mm) ¹¹ | 145 | °C | ISO 75/Ae |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 65 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 65 | °C | UL 746B |
Table 4 of 6
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, at 23°C) ¹¹ | 505 | J/m | ASTM D4812 |
| Izod Impact (Unnotched, at -30°C) ¹¹ | 465 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 85 | J/m | ASTM D256 |
| Izod Impact (Notched, at -30°C) ¹¹ | 75 | J/m | ASTM D256 |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 30 | kJ/m² | ISO 180/1U |
| Izod Impact (Unnotched, 80*10*4, at -30°C) ¹¹ | 30 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 8 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at -30°C) ¹¹ | 7 | kJ/m² | ISO 180/1A |
| Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 10 | kJ/m² | ISO 179/1eA |
| Charpy Impact (at -30°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 9 | kJ/m² | ISO 179/1eA |
| Charpy Impact (at 23°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹ | 30 | kJ/m² | ISO 179/1eU |
| Charpy Impact (at -30°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹ | 30 | kJ/m² | ISO 179/1eU |
Table 5 of 6
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 100 - 120 | °C |
| Drying Time ⁷ | 2 - 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 290 - 320 | °C |
| Nozzle Temperature ⁷ | 290 - 320 | °C |
| Front - Zone 3 Temperature ⁷ | 300 - 310 | °C |
| Middle - Zone 2 Temperature ⁷ | 280 - 300 | °C |
| Rear - Zone 1 Temperature ⁷ | 270 - 280 | °C |
| Hopper Temperature ⁷ | 60 - 80 | °C |
| Mold Temperature ⁷ | 80 - 120 | °C |
Table 6 of 6
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Glow Wire Flammability Index (at 1.5 mm) ᵖ | 800 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index (at 3 mm) ᵖ | 775 | °C | IEC 60695-2-12 |
| Glow Wire Ignitability Temperature (at 1.5 mm) ᵖ | 800 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature (at 3.0 mm) ᵖ | 800 | °C | IEC 60695-2-13 |
| UL Recognized (94HB Flame Class Rating) ᵖ | min. 1.5 | mm | UL 94 |