SABIC's Specialties Business NORYL ZM3640 resin is a mineral reinforced blend of polyphenylene ether (PPE) + polystyrene (PS). This grade contains non-brominated, non-chlorinated flame retardant and has a UL94 flame rating of V1 at 1.5mm. NORYL ZM3640 resin exhibits high heat resistance, low warpage, good dimensional stability and is an excellent candidate for printer chassis applications. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Electronics
- Displays
- Connectors
Product Families
- Blends & Alloys
Other characteristics
- Brand
- NORYL™ Resin
- Density
- 1220.0 - 1220.0 kg/m³
- Polymer Name
- PPO/PS Alloy
- Processing Methods
- Injection Molding
- Note
ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Consumer Goods
- Electrical & Electronics
- Flame Rating
- UL 94 V1
- Technology
- Plastics
- Labeling Claims
- Bromine-free
- Chlorine-free
- No Added PFAS
- Fillers Included
- Mineral
- Additives Included
- Flame Retardant
- Mold Release Agent
- Material Features
- Amorphous
- Dimensional Stability
- Flame Retardant
- Good Mold Release
- Good Processability
- Good Stiffness
- High Hydrolytic Stability
- High Stiffness
- Country Availability
- China (Mainland)
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Cell Phones
- Computer Components
- Connectors
- Displays
- Electrical/Electronic Applications
- Printer Parts
- Tablets
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 5 mm/min) ¹¹ | 60 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 4 | % | ASTM D638 |
| Flexural Stress (Yield, at 6.4 mm) ¹¹ | 102 | MPa | ASTM D790 |
| Flexural Modulus (at 6.4 mm) ¹¹ | 4620 | MPa | ASTM D790 |
Table 2 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.22 | — | ASTM D792 |
| Melt Flow Rate (at 300°C, 2.16 kgf) ¹¹ | 24 | g/10 min | ASTM D1238 |
Table 3 of 6
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 103 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000042 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000048 | 1/°C | ASTM E831 |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 65 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 65 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 65 | °C | UL 746B |
Table 4 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 35 | J/m | ASTM D256 |
Table 5 of 6
14 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 90 - 95 | °C |
| Drying Time ⁷ | 3 - 4 | Hrs |
| Drying Time (Cumulative) ⁷ | 8 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 255 - 280 | °C |
| Nozzle Temperature ⁷ | 255 - 280 | °C |
| Front - Zone 3 Temperature ⁷ | 245 - 280 | °C |
| Middle - Zone 2 Temperature ⁷ | 230 - 275 | °C |
| Rear - Zone 1 Temperature ⁷ | 220 - 270 | °C |
| Mold Temperature ⁷ | 65 - 90 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed ⁷ | 20 - 100 | rpm |
Table 6 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94V-1 Flame Class Rating) ʳ | min. 1.5 | mm | UL 94 |