NORYL™ Resin EM6100
SABIC's Specialties Business NORYL™ EM6100 is a non-reinforced blend of polyphenylene ether (PPE) + polystyrene (PS). This grade exhibits a balance of flow/heat/impact, dimensional stability, along with paint adhesion. NORYL™ EM6100 resin is suitable for the automotive interior market in applications such as HVAC housings and radio components. MS-DB424, WSBM4D844-A9, GMP.PPE.007. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Interior
Product Families
- Blends & Alloys
Other characteristics
- Brand
- NORYL™ Resin
- Density
- 1050.0 - 1050.0 kg/m³
- Polymer Name
- PPO/PS Alloy
- Flexural Modulus
- 2100.0 - 2100.0 MPa
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Automotive & Transportation
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Additives Included
- Anti-Static Agent
- Impact Modifier
- Mold Release Agent
- Material Features
- Amorphous
- Anti-Static
- Dimensional Stability
- Good Mold Release
- High Hydrolytic Stability
- Impact Modified
- Low Moisture Absorption
- Low Shrinkage
- Country Availability
- Canada
- Mexico
- USA
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Automotive Interior Parts
- Automotive Interior Trim
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
16 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break) ¹¹ | 40 | MPa | ASTM D638 |
| Tensile Stress (Break) ¹¹ | 40 | MPa | ISO 527 |
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 43 | MPa | ASTM D638 |
| Tensile Strain (Yield) ¹¹ | 2.8 | % | ISO 527 |
| Tensile Strain (Yield) ¹¹ | 3 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 65 | % | ASTM D638 |
| Tensile Modulus (at 5 mm/min) ¹¹ | 1900 | MPa | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 67 | MPa | ASTM D790 |
| Flexural Stress (Yield, 2.6 mm/min, 100 mm span) ¹¹ | 66 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2100 | MPa | ASTM D790 |
| Flexural Modulus (at 2.6 mm/min, 100 mm span) ¹¹ | 2000 | MPa | ASTM D790 |
| Tensile Stress (Yield) ¹¹ | 42 | MPa | ISO 527 |
Table 2 of 6
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.05 | — | ASTM D792 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.2 | % | ASTM D570 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.5 - 0.7 | % | SABIC method |
| Melt Flow Rate (at 280°C, 5.0 kgf) ¹¹ | 15 | g/10 min | ASTM D1238 |
| Melt Volume Rate (at 280°C, 5.0 kg) ¹¹ | 15 | cm³/10 min | ISO 1133 |
Table 3 of 6
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 124 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 106 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 115 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at 0°C to 100°C, flow) ¹¹ | 0.000117 | 1/°C | ASTM E831 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 119 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/120) ¹¹ | 123 | °C | ISO 306 |
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 126 | °C | ISO 75/Bf |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 110 | °C | ISO 75/Af |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 65 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 65 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 65 | °C | UL 746B |
Table 4 of 6
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 453 | J/m | ASTM D256 |
| Izod Impact (Notched, at -30°C) ¹¹ | 250 | J/m | ASTM D256 |
| Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹ | 36 | J | ASTM D3763 |
| Instrumented Dart Impact Energy (Peak, at -30°C) ¹¹ | 24 | J | ASTM D3763 |
| Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 42 | J | ASTM D3763 |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 33 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at -30°C) ¹¹ | 15 | kJ/m² | ISO 180/1A |
| Charpy Impact (Notched, at 23°C) ¹¹ | 33 | kJ/m² | ISO 179/2C |
| Charpy Impact (Notched, at -30°C) ¹¹ | 19 | kJ/m² | ISO 179/2C |
Table 5 of 6
14 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 95 - 105 | °C |
| Drying Time ⁷ | 3 - 4 | Hrs |
| Drying Time (Cumulative) ⁷ | 8 | Hrs |
| Maximum Moisture Content ⁷ | 2.00E-02 | % |
| Melt Temperature ⁷ | 265 - 295 | °C |
| Nozzle Temperature ⁷ | 265 - 295 | °C |
| Front - Zone 3 Temperature ⁷ | 255 - 295 | °C |
| Middle - Zone 2 Temperature ⁷ | 245 - 290 | °C |
| Rear - Zone 1 Temperature ⁷ | 230 - 280 | °C |
| Mold Temperature ⁷ | 65 - 95 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed ⁷ | 20 - 100 | rpm |
Table 6 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94HB Flame Class Rating) ᵖ | min. 1.5 | mm | UL 94 |