NORYL™ Resin EN265
SABIC's Specialties Business NORYL™ EN265 resin is a non-reinforced blend of polyphenylene ether (PPE) + polystyrene (PS). This high heat extrusion grade contains non-brominated, non-chlorinated flame retardant and carries a UL94 flame rating of v0 at 6mm and V1 at 1.5mm along with UL746C outdoor weatherability rating of F1. NORYL™ EN265 resin exhibits excellent impact strength, very low moisture absorption, good dimensional stability, and great machinability. NORYL™ EN265 resin is an excellent candidate for a variety of indoor and outdoor electrical applications including trunking and conduit. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Electronics
- Displays
- Circuit Breakers
- Conduits & Cable Management
- Connectors
- Switches & Relays
Product Families
- Blends & Alloys
Other characteristics
- Brand
- NORYL™ Resin
- Density
- 1080.0 - 1080.0 kg/m³
- Polymer Name
- PPO/PS Alloy
- Processing Methods
- Extrusion
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Consumer Goods
- Electrical & Electronics
- Flame Rating
- UL 94 V0
- UL 94 V1
- Technology
- Plastics
- Labeling Claims
- Bromine-free
- Chlorine-free
- No Added PFAS
- Additives Included
- Flame Retardant
- Heat Stabilizer
- Material Features
- Amorphous
- Dimensional Stability
- Flame Retardant
- Good Extrusion Properties
- Heat Stabilized
- High Hydrolytic Stability
- Low Moisture Absorption
- Low Shrinkage
- Country Availability
- Canada
- Mexico
- USA
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Cell Phones
- Computer Components
- Conduit
- Connectors
- Displays
- Electrical Components
- Electrical/Electronic Applications
- Enclosure
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
Technical data
Table 1 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 63 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 25 | % | ASTM D638 |
| Flexural Stress (Yield, 2.6 mm/min, 100 mm span) ¹¹ | 99 | MPa | ASTM D790 |
| Flexural Modulus (at 2.6 mm/min, 100 mm span) ¹¹ | 2550 | MPa | ASTM D790 |
| Hardness (Rockwell R) ¹¹ | 119 | — | ASTM D785 |
Table 2 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.08 | — | ASTM D792 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.07 | % | ASTM D570 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.5 - 0.7 | % | SABIC method |
Table 3 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 123 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 95°C, flow) ¹¹ | 0.0000594 | 1/°C | ASTM E831 |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 110 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 105 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 110 | °C | UL 746B |
Table 4 of 7
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Dielectric Strength (in oil, at 3.2mm) ¹¹ | 19.6 | kV/mm | ASTM D149 |
| Relative Permittivity (50/60 Hz) ¹¹ | 2.69 | — | ASTM D150 |
| Dissipation Factor (at 50/60 Hz) ¹¹ | 0.0007 | — | ASTM D150 |
| Comparative Tracking Index (UL, PLC) ¹¹ | 1 | PLC Code | UL 746A |
| High Ampere Arc Ignition (PLC 0) ¹¹ | min. 1.5 | mm | UL 746A |
| Hot Wire Ignition (PLC 0) ¹¹ | min. 1.5 | mm | UL 746A |
| High Voltage Arc Track Rate (PLC) ¹¹ | 4 | PLC Code | UL 746A |
| Arc Resistance (Tungsten, PLC) ¹¹ | 6 | PLC Code | ASTM D495 |
Table 5 of 7
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Adapter Temperature | 250 | °C |
| Barrel - Zone 1 Temperature | 205 | °C |
| Barrel - Zone 2 Temperature | 205 | °C |
| Barrel - Zone 3 Temperature | 225 | °C |
| Barrel - Zone 4 Temperature | 225 | °C |
| Die Temperature | 250 | °C |
| Drying Temperature | 105 - 115 | °C |
| Drying Time | 2 - 4 | Hrs |
| Drying Time (Cumulative) | 8 | Hrs |
| Melt Temperature | 225 - 255 | °C |
Table 6 of 7
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 186 | J/m | ASTM D256 |
| Izod Impact (Notched, at -40°C) ¹¹ | 133 | J/m | ASTM D256 |
| Color (at -30°C) ¹¹ | 14 | J | ASTM D3029 |
| Color (at -40°C) ¹¹ | 4 | J | ASTM D3029 |
Table 7 of 7
13 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Oxygen Index (LOI) ʳ | 2.92E+01 | % | ASTM D2863 |
| Radiant Panel Listing ʳ | RP100 | — | UL Tested |
| UV-light (Water exposure/immersion) ʳ | F1 | — | UL 746C |
| Glow Wire Flammability Index (at 1 mm) ʳ | 900 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index (at 1.5 mm) ʳ | 900 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index (at 2 mm) ʳ | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index (at 3 mm) ʳ | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignitability Temperature (at 1.0 mm) ʳ | 700 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature (at 1.5 mm) ʳ | 700 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature (at 2.0 mm) ʳ | 725 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature (at 3.0 mm) ʳ | 725 | °C | IEC 60695-2-13 |
| UL Recognized (94V-0 Flame Class Rating) ʳ | min. 6 | mm | UL 94 |