NORYL GTX™ Resin GTX951W
SABIC's Specialties Business NORYL GTX951W resin is a non-reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This injection moldable grade exhibits high heat resistance, excellent chemical resistance, high melt flow, and added mold release. NORYL GTX951W resin was designed for automotive under-the-hood applications such as power distribution boxes, relay boxes, and junction boxes. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Automotive Lighting
- Electrical & Electronic Systems
- Powertrain & UTH
- Interior Fixtures
- Automotive Electronics
- Lighting
- Batteries
- Connectors
- Housings & Enclosures
- Sensors & Actuators
Product Families
- Blends & Alloys
Other characteristics
- Brand
- NORYL GTX™ Resin
- Density
- 1100.0 - 1100.0 kg/m³
- Polymer Name
- PPO/Nylon Alloy
- Flexural Modulus
- 2370.0 - 2370.0 MPa
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- Markets
- Automotive & Transportation
- Building & Construction
- Electrical & Electronics
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Additives Included
- Heat Stabilizer
- Impact Modifier
- Mold Release Agent
- Material Features
- Chemical Resistant
- Dimensional Stability
- Good Mold Release
- Heat Stabilized
- High Hydrolytic Stability
- High Impact Resistance
- High Stiffness
- High Tensile Strength
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Automotive Electronics
- Automotive Under The Hood
- Back Panel
- Battery Cover
- Connectors
- Corner Support Plates
- Crash Protection
- Electrical/Electronic Applications
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
13 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 65 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 55 | % | ASTM D638 |
| Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 57 | MPa | ASTM D638 |
| Flexural Stress (Yield, 2.6 mm/min, 100 mm span) ¹¹ | 100 | MPa | ASTM D790 |
| Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ | 5 | % | ASTM D638 |
| Flexural Modulus (at 2.6 mm/min, 100 mm span) ¹¹ | 2550 | MPa | ASTM D790 |
| Flexural Modulus (at 2.6 mm/min, 100 mm span) ¹¹ | 2450 | MPa | ASTM D790 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 2250 | MPa | ASTM D638 |
| Flexural Stress (Break, 2.6 mm/min, 100 mm span) ¹¹ | 100 | MPa | ASTM D790 |
| Tensile Stress (Yield, 50 mm/min) ¹¹ | 66 | MPa | ISO 527 |
| Tensile Strain (Break, 50 mm/min) ¹¹ | 51 | % | ISO 527 |
| Flexural Stress (Break, 2 mm/min) ¹¹ | 98 | MPa | ISO 178 |
Table 2 of 7
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.1 | — | ASTM D792 |
| Melt Flow Rate (at 280°C, 2.16 kgf) ¹¹ | 24 | g/10 min | ASTM D1238 |
| Melt Flow Rate (at 280°C, 5.0 kgf) ¹¹ | 65 | g/10 min | ASTM D1238 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 1.4 - 1.7 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 1.2 - 1.5 | % | ASTM D955 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 1.99 | % | ISO 62-1 |
| Moisture Absorption (at 23°C, 50% RH, Equilibrium) ¹¹ | 0.39 | % | ISO 62-4 |
Table 3 of 7
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 0.45 MPa, 6.4 mm, Unannealed) ¹¹ | 195 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.00009 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000085 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at 60°C to 138°C, flow) ¹¹ | 0.000167 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at 60°C to 138°C, xflow) ¹¹ | 0.000153 | 1/°C | ASTM E831 |
| Heat Deflection Temperature/Be (at 0.45MPa, Edgew 120*10*4, sp=100mm) ¹¹ | 181 | °C | ISO 75/Be |
Table 4 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Dielectric Strength (in oil, at 1.6mm) ¹¹ | 22.4 | kV/mm | ASTM D149 |
| Dissipation Factor (at at 1 MHz) ¹¹ | 0.017 | — | ASTM D150 |
Table 5 of 7
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 211 | J/m | ASTM D256 |
| Izod Impact (Notched, at -30°C) ¹¹ | 100 | J/m | ASTM D256 |
| Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹ | 48 | J | ASTM D3763 |
| Instrumented Dart Impact Energy (Peak, at -30°C) ¹¹ | 32 | J | ASTM D3763 |
| Izod Impact (Notched, 63.5*12.7*3.2, at 23°C) ¹¹ | 13 | kJ/m² | ISO 180/4A |
| Izod Impact (Notched, 63.5*12.7*3.2, at -30°C) ¹¹ | 8 | kJ/m² | ISO 180/4A |
| Charpy Impact (Notched, at 23°C) ¹¹ | 21 | kJ/m² | ISO 179/2C |
| Charpy Impact (Notched, at -20°C) ¹¹ | 10 | kJ/m² | ISO 179/2C |
Table 6 of 7
24 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 100 - 120 | °C |
| Drying Temperature ⁷ | 95 - 105 | °C |
| Drying Time ⁷ | 3 - 4 | Hrs |
| Drying Time ⁷ | 2 - 3 | Hrs |
| Drying Time (Cumulative) ⁷ | 8 | Hrs |
| Maximum Moisture Content ⁷ | 0.07 | % |
| Melt Temperature ⁷ | 280 - 310 | °C |
| Melt Temperature ⁷ | 270 - 295 | °C |
| Minimum Moisture Content ⁷ | 0.02 | % |
| Nozzle Temperature ⁷ | 270 - 300 | °C |
| Nozzle Temperature ⁷ | 270 - 295 | °C |
| Front - Zone 3 Temperature ⁷ | 280 - 300 | °C |
Table 7 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94HB Flame Class Rating) ᵖ | 1.2 | mm | UL 94 |