NORYL GTX™ Resin GTX6009

Name: NORYL GTX™ Resin GTX6009
Brand: NORYL GTX™ Resin

SABIC's Specialties Business NORYL GTX™ Resin GTX6009 resin is an injection moldable, non-reinforced alloy consisting of polyphenylene ether (PPE) and polyamide (PA). It features high heat resistance and excellent chemical resistance, making it a possible candidate for exterior automotive applications such as wheel covers and wheel trim. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.

Product families

Applications

Automotive & Transportation — Automotive

Electrical & Electronic Systems
Exterior & Body

Electrical & Electronics — Parts & Components

Batteries
Housings & Enclosures

Product Families

Plastics — Engineering & Specialty Polymers

Blends & Alloys

Other characteristics

Brand: NORYL GTX™ Resin
Density: 1120.0 - 1120.0 kg/m³
Polymer Name: PPO/Nylon Alloy
Processing Methods: Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Markets: Automotive & Transportation
Electrical & Electronics
Technology: Plastics
Labeling Claims: No Added PFAS
Additives Included: Impact Modifier
Mold Release Agent
Material Features: Chemical Resistant
Creep Resistant
Dimensional Stability
Good Mold Release
High Hydrolytic Stability
High Impact Resistance
High Stiffness
High Tensile Strength
Country Availability: China (Mainland)
Plastics and Elastomers End Uses: Automotive Exterior Parts
Back Panel
Battery Cover
Corner Support Plates
Crash Protection
Front Panel
Rocker Reinforcement
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 6

5 rows

Characteristic	Value	Unit	Method
Tensile Stress (Yield, Type I, 50 mm/min) ¹¹	53	MPa	ASTM D638
Tensile Strain (Break, Type I, 50 mm/min) ¹¹	90	%	ASTM D638
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹	81	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	2130	MPa	ASTM D790
Hardness (Rockwell R) ¹¹	110	—	ASTM D785

Table 2 of 6

3 rows

Characteristic	Value	Unit	Method
Specific Gravity ¹¹	1.12	—	ASTM D792
Water Absorption (at 23°C, 24hrs) ¹¹	0.5	%	ASTM D570
Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹	1.2 - 1.3	%	SABIC method

Table 3 of 6

2 rows

Characteristic	Value	Unit	Method
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	160	°C	ASTM D648
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.000068 - 0.000079	1/°C	ASTM E831

Table 4 of 6

1 row

Characteristic	Value	Unit	Method
Volume Resistivity ¹¹	1.00E+16	Ω.cm	ASTM D257

Table 5 of 6