LNP™ VERTON™ Compound RX06424

Chemical Family: Polyamides

LNP™ VERTON™ Compound RX06424 incorporates Polyamide 66 (nylon 66) resin with a high content of 60% long glass fiber, enhancing its mechanical properties significantly. Designed for easy molding, this compound offers manufacturers efficiency and versatility in processing. It is heat stabilized and UV stabilized, ensuring prolonged durability and performance in challenging environmental conditions. The structural reinforcement of LNP™ VERTON™ Compound RX06424 makes it suitable for applications where strength and reliability are critical, such as automotive components, industrial machinery, and outdoor equipment. This compound strikes a balance between robust mechanical strength, dimensional stability, and resistance to weathering, making it an excellent choice for demanding engineering applications requiring high-performance materials.

Product families

Applications

Consumer Goods — Appliances & Electronics
Consumer Goods — Sports & Recreation

Automotive & Transportation — Automotive

Exterior & Body

Building & Construction — Building Materials

Structural Components

Electrical & Electronics — Devices & Assemblies

Industrial Automation

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Other characteristics

Brand: LNP™ VERTON™ Compound
Polymer Name: Polyamide 66 (PA 66)
Fillers Included: Glass Fiber
Processing Methods: Injection Molding
Note: (1) The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design. (2) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article. (3) Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wallmolding and gas-assist molding.
Markets: Automotive & Transportation
Building & Construction
Consumer Goods
Electrical & Electronics
Technology: Plastics
Labeling Claims: No Added PFAS
Material Features: Easy To Mold
Good Processability
Good UV Stability
Good Weather Stability
Heat Stabilized
High Stiffness
High Strength
UV Stabilized
Plastics and Elastomers End Uses: Automotive Exterior Parts
Building Materials
Commercial Appliance
Home Appliances
Sporting Goods
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 5

10 rows

Characteristic	Value	Unit	Method
Tensile Strain (Break) ¹	1.6	%	ISO 527
Tensile Strain (Break) ¹	1.6	%	ASTM D638
Tensile Modulus (at 50 mm/min) ¹	19650.0	MPa	ASTM D638
Flexural Stress ¹	433.0	MPa	ISO 178
Flexural Stress ¹	430.0	MPa	ASTM D790
Flexural Modulus ¹	18920.0	MPa	ISO 178
Flexural Modulus ¹	18020.0	MPa	ASTM D790
Tensile Stress (Break) ¹	261.0	MPa	ISO 527
Tensile Stress (Break) ¹	270.0	MPa	ASTM D638
Tensile Modulus (at 1 mm/min) ¹	23280.0	MPa	ISO 527

Table 2 of 5

7 rows

Characteristic	Value	Unit	Method
Density ¹	1.71	g/cm³	ISO 1183
Density ¹	1.71	g/cm³	ASTM D792
Moisture Absorption (23°C/50% RH/24 hrs) ¹	0.44	%	ASTM D570
Mold Shrinkage (flow, 24 hrs) ²	0.2	%	ASTM D955
Mold Shrinkage (flow, 24 hrs) ²	0.2	%	ISO 294
Mold Shrinkage (xflow, 24 hrs) ²	0.4	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ²	0.4	%	ISO 294

Table 3 of 5