LNP™ VERTON™ Compound RV00AEX5
- Chemical Family
- Polyamides
LNP™ VERTON™ Compound RV00AEX5 consists of Polyamide 66 (nylon 66) resin infused with 50% long glass fiber, offering a robust solution for structural applications. It boasts easy molding characteristics, facilitating efficient manufacturing processes without compromising on strength and durability. This compound is well-suited for a variety of industries including automotive, industrial, and consumer goods, where high mechanical performance is crucial. LNP™ VERTON™ Compound RV00AEX5 delivers superior stiffness and structural integrity, making it an ideal choice for components requiring both reliability and ease of production.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Sports & Recreation
- Exterior & Body
- Structural Components
- Industrial Automation
Product Families
- Polyamides
Other characteristics
- Brand
- LNP™ VERTON™ Compound
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- Glass Fiber
- Processing Methods
- Injection Molding
- Note
(1) The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design. (2) UL Ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card. (3) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article. (4) Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Easy To Mold
- Good Processability
- Heat Stabilized
- High Stiffness
- High Strength
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Automotive Exterior Parts
- Building Materials
- Commercial Appliance
- Home Appliances
- Sporting Goods
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, 5 mm/min) ¹ | 276.0 | MPa | ISO 527 |
| Tensile Stress (Break, 5 mm/min) ¹ | 276.0 | MPa | ISO 527 |
| Tensile Strain (Yield, 5 mm/min) ¹ | 2.0 | % | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹ | 2.0 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹ | 17800.0 | MPa | ISO 527 |
| Flexural Stress (Yield, 2 mm/min) ¹ | 366.0 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹ | 15000.0 | MPa | ISO 178 |
Table 2 of 7
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mold Shrinkage (flow, 24 hrs) ³ | 0.3 | % | ISO 294 |
| Mold Shrinkage (xflow, 24 hrs) ³ | 0.8 | % | ISO 294 |
| Density ¹ | 1.6 | g/cm³ | ISO 1183 |
| Water Absorption (23°C/24hrs) ¹ | 0.9 | % | ISO 62-1 |
Table 3 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature/Bf (0.45 MPa Flatw 80*10*4 sp=64mm) ¹ | 259.0 | °C | ISO 75/Bf |
| Heat Deflection Temperature/Af (1.8 MPa Flatw 80*10*4 sp=64mm) ¹ | 256.0 | °C | ISO 75/Af |
| Relative Temperature Index (Elec) ² | 105.0 | °C | UL 746B |
| Relative Temperature Index (Mech with impact) ² | 110.0 | °C | UL 746B |
| Relative Temperature Index (Mech w/o impact) ² | 110.0 | °C | UL 746B |
Table 4 of 7
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Comparative Tracking Index (UL) ² | 0.0 | PLC Code | UL 746A |
| Hot-Wire Ignition (HWI, PLC 0) ² | 1.5 | mm | UL 746A |
| Hot-Wire Ignition (HWI, PLC 2) ² | 0.75 | mm | UL 746A |
| High Amp Arc Ignition (HAI, PLC 0) ² | 0.75 | mm | UL 746A |
| High Voltage Arc Track Rate ² | 0.0 | PLC Code | UL 746A |
| Arc Resistance (Tungsten) ² | 6.0 | PLC Code | ASTM D495 |
Table 5 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched 80*10*4 +23°C) ¹ | 90.0 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched 80*10*4 +23°C) ¹ | 45.0 | kJ/m² | ISO 180/1A |
Table 6 of 7
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁴ | 80.0 | °C |
| Drying Time ⁴ | 4.0 | Hrs |
| Maximum Moisture Content ⁴ | 0.15 - 0.25 | % |
| Melt Temperature ⁴ | 290 - 305 | °C |
| Front - Zone 3 Temperature ⁴ | 290 - 300 | °C |
| Middle - Zone 2 Temperature ⁴ | 290 - 300 | °C |
| Rear - Zone 1 Temperature ⁴ | 280 - 295 | °C |
| Mold Temperature ⁴ | 95 - 110 | °C |
| Back Pressure ⁴ | 0.2 - 0.3 | MPa |
| Screw Speed ⁴ | 30 - 60 | rpm |
Table 7 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized 94HB Flame Class Rating ² | min. 0.75 | mm | UL 94 |