LNP™ VERTON™ Compound RV00CE
- Chemical Family
- Polyamides
LNP™ VERTON™ Compound RV00CE is formulated with Polyamide 66 (nylon 66) resin incorporating 60% long glass fiber, enhancing its structural integrity. This compound is tailored for applications requiring both strength and ease of molding, making it suitable for a wide range of industrial uses. Its high glass fiber content ensures superior mechanical properties, including high stiffness and impact resistance, essential for demanding environments. LNP™ VERTON™ Compound RV00CE is particularly well-suited for components in automotive, aerospace, and industrial sectors where performance under load and dimensional stability are critical. With its advanced formulation, this compound facilitates efficient production processes while maintaining excellent product consistency and reliability.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Sports & Recreation
- Exterior & Body
- Structural Components
- Industrial Automation
Product Families
- Polyamides
Other characteristics
- Brand
- LNP™ VERTON™ Compound
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- Glass Fiber
- Processing Methods
- Injection Molding
- Note
(1) The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design. (2) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article. (3) Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Easy To Mold
- Good Processability
- High Stiffness
- High Strength
- Plastics and Elastomers End Uses
- Automotive Exterior Parts
- Building Materials
- Commercial Appliance
- Home Appliances
- Sporting Goods
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break) ¹ | 261.0 | MPa | ISO 527 |
| Tensile Strain (Break) ¹ | 1.6 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹ | 23280.0 | MPa | ISO 527 |
| Flexural Stress ¹ | 433.0 | MPa | ISO 178 |
| Flexural Modulus ¹ | 18920.0 | MPa | ISO 178 |
Table 2 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mold Shrinkage (flow, 24 hrs) ² | 0.2 | % | ISO 294 |
| Mold Shrinkage (xflow, 24 hrs) ² | 0.41 | % | ISO 294 |
| Density ¹ | 1.71 | g/cm³ | ISO 1183 |
Table 3 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹ | 1.7e-05 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹ | 5.3e-05 | 1/°C | ISO 11359-2 |
| Heat Deflection Temperature/Af (1.8 MPa Flatw 80*10*4 sp=64mm) ¹ | 252.0 | °C | ISO 75/Af |
Table 4 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched 80*10*4 +23°C) ¹ | 102.0 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched 80*10*4 +23°C) ¹ | 54.0 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched 80*10*4 -40°C) ¹ | 43.0 | kJ/m² | ISO 180/1A |
Table 5 of 5
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ³ | 80.0 | °C |
| Drying Time ³ | 4.0 | Hrs |
| Maximum Moisture Content ³ | 0.15 - 0.25 | % |
| Melt Temperature ³ | 290 - 305 | °C |
| Front - Zone 3 Temperature ³ | 290 - 300 | °C |
| Middle - Zone 2 Temperature ³ | 290 - 300 | °C |
| Rear - Zone 1 Temperature ³ | 280 - 295 | °C |
| Mold Temperature ³ | 95 - 110 | °C |
| Back Pressure ³ | 0.2 - 0.3 | MPa |
| Screw Speed ³ | 30 - 60 | rpm |