LNP™ VERTON™ Compound RV0079SS
- Chemical Family
- Polyamides
LNP™ VERTON™ Compound RV0079SS integrates Polyamide 66 (Nylon 66) resin with 35% long glass fiber, featuring flame retardant, heat stabilized, and structural properties. Engineered for demanding applications in automotive exteriors, building components, and across sport, leisure, home appliances, and commercial appliances sectors, this compound ensures high stiffness and strength while maintaining excellent processability during injection molding. With a focus on sustainability and safety, LNP™ VERTON™ Compound RV0079SS does not include intentionally added PFAS, offering reliable performance in environments requiring flame retardancy and structural integrity.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Sports & Recreation
- Exterior & Body
- Equipment & Parts
- Consumer Electronics
Product Families
- Polyamides
Other characteristics
- Brand
- LNP™ VERTON™ Compound
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- Glass Fiber
- Additives Included
- Flame Retardant
- Processing Methods
- Injection Molding
- Note
¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design. ² Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article. ³ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Industrial
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Good Processability
- Heat Stabilized
- High Stiffness
- High Strength
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Automotive Applications
- Commercial Appliance
- Construction Applications
- Home Appliances
- Water Management
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break) ¹ | 213.0 | MPa | ISO 527 |
| Tensile Stress (Break, 5 mm/min) ¹ | 213.0 | MPa | ISO 527 |
| Tensile Strain (Break) ¹ | 1.8 | % | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹ | 1.8 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹ | 15070.0 | MPa | ISO 527 |
| Flexural Stress ¹ | 298.0 | MPa | ISO 178 |
| Flexural Stress (Yield, 2 mm/min) ¹ | 298.0 | MPa | ISO 178 |
| Flexural Modulus ¹ | 13280.0 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹ | 13280.0 | MPa | ISO 178 |
Table 2 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹ | 1.69 | g/cm³ | ISO 1183 |
Table 3 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature/Bf (0.45 MPa Flatw 80*10*4 sp=64mm) ¹ | 262.0 | °C | ISO 75/Bf |
| Heat Deflection Temperature/Af (1.8 MPa Flatw 80*10*4 sp=64mm) ¹ | 259.0 | °C | ISO 75/Af |
| Relative Temperature Index (Elec) ² | 130.0 | °C | UL 746B |
| Relative Temperature Index (Mech with impact) ² | 105.0 | °C | UL 746B |
| Relative Temperature Index (Mech w/o impact) ² | 115.0 | °C | UL 746B |
Table 4 of 7
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Comparative Tracking Index (UL) ² | 3.0 | PLC Code | UL 746A |
| Hot-Wire Ignition (HWI, PLC 0) ² | min. 3 | mm | UL 746A |
| Hot-Wire Ignition (HWI, PLC 1) ² | min. 1.7 | mm | UL 746A |
| High Amp Arc Ignition (HAI, PLC 0) ² | min. 3 | mm | UL 746A |
| High Amp Arc Ignition (HAI, PLC 1) ² | min. 1.7 | mm | UL 746A |
| High Voltage Arc Track Rate ² | 1.0 | PLC Code | UL 746A |
| Arc Resistance (Tungsten) ² | 7.0 | PLC Code | ASTM D495 |
Table 5 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched 80*10*4 +23°C) ¹ | 57.0 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched 80*10*4 +23°C) ¹ | 32.0 | kJ/m² | ISO 180/1A |
Table 6 of 7
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Drying Temperature ³ | 80.0 | °C | UL 94 |
| Drying Time ³ | 4.0 | Hrs | — |
| Maximum Moisture Content ³ | 0.15 - 0.25 | % | — |
| Melt Temperature ³ | 290 - 305 | °C | — |
| Front - Zone 3 Temperature ³ | 290 - 300 | °C | — |
| Middle - Zone 2 Temperature ³ | 290 - 300 | °C | — |
| Rear - Zone 1 Temperature ³ | 280 - 295 | °C | — |
| Mold Temperature ³ | 95 - 110 | °C | — |
| Back Pressure ³ | 0.2 - 0.3 | MPa | — |
| Screw Speed ³ | 30 - 60 | rpm | — |
Table 7 of 7
1 row| Characteristic | Value | Unit |
|---|---|---|
| UL Recognized 94V-0 Flame Class Rating ² | min. 1.7 | mm |