LNP™ VERTON™ Compound PX00700
- Chemical Family
- Polyamides
LNP™ VERTON™ Compound PX00700 combines Polyamide 6 (Nylon 6) resin with 35% long glass fiber and proprietary fillers, emphasizing structural strength. Tailored for demanding applications in automotive exteriors, building components, and various industrial uses, this compound offers high stiffness and strength without intentional PFAS additives. Its composition includes both glass fiber and proprietary fillers, optimizing performance and durability during injection molding processes. LNP™ VERTON™ Compound PX00700 is engineered to withstand rigorous environments, making it suitable for sport and leisure equipment, home appliances, and commercial appliances where robustness and reliability are essential.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Sports & Recreation
- Exterior & Body
- Equipment & Parts
- Consumer Electronics
Product Families
- Polyamides
Other characteristics
- Brand
- LNP™ VERTON™ Compound
- Polymer Name
- Polyamide 6 (PA 6)
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 8210.0 - 8210.0 MPa
- Processing Methods
- Injection Molding
- Note
¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design. ² Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Industrial
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- High Stiffness
- High Strength
- Plastics and Elastomers End Uses
- Automotive Applications
- Commercial Appliance
- Construction Applications
- Home Appliances
- Water Management
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break) ¹ | 188.0 | MPa | ISO 527 |
| Tensile Strain (Break) ¹ | 2.7 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹ | 9510.0 | MPa | ISO 527 |
| Flexural Stress ¹ | 249.0 | MPa | ISO 178 |
| Flexural Modulus ¹ | 8210.0 | MPa | ISO 178 |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹ | 1.38 | g/cm³ | ISO 1183 |
Table 3 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature/Bf (0.45 MPa Flatw 80*10*4 sp=64mm) ¹ | 214.0 | °C | ISO 75/Bf |
| Heat Deflection Temperature/Af (1.8 MPa Flatw 80*10*4 sp=64mm) ¹ | 210.0 | °C | ISO 75/Af |
Table 4 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched 80*10*4 +23°C) ¹ | 73.0 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched 80*10*4 +23°C) ¹ | 31.0 | kJ/m² | ISO 180/1A |
Table 5 of 5
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ² | 80.0 | °C |
| Drying Time ² | 4.0 | Hrs |
| Maximum Moisture Content ² | 0.15 - 0.25 | % |
| Melt Temperature ² | 265 - 275 | °C |
| Front - Zone 3 Temperature ² | 275 - 290 | °C |
| Middle - Zone 2 Temperature ² | 265 - 275 | °C |
| Rear - Zone 1 Temperature ² | 250 - 260 | °C |
| Mold Temperature ² | 80 - 95 | °C |
| Back Pressure ² | 0.3 - 0.7 | MPa |
| Screw Speed ² | 30 - 60 | rpm |