LNP™ VERTON™ Compound MV00CS
- Chemical Family
- PolyolefinsPolypropylenes (PP)
LNP™ VERTON™ Compound MV00CS features a polypropylene (PP) resin fortified with 60% long glass fibers, ensuring exceptional structural integrity and stiffness. This compound is chemically coupled for enhanced performance, heat stabilized to maintain strength under varying temperatures, and tailored for structural applications. With no intentionally added PFAS, it meets stringent environmental standards. Ideal for automotive exteriors, water management systems, sport and leisure equipment, home appliances, and commercial appliances, LNP™ VERTON™ Compound MV00CS offers robust mechanical properties suitable for a wide range of industrial applications. It excels in injection molding processes, delivering reliable performance and dimensional stability in demanding environments.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Sports & Recreation
- Exterior & Body
- Equipment & Parts
- Consumer Electronics
Product Families
- Polyolefins
Other characteristics
- Brand
- LNP™ VERTON™ Compound
- Polymer Name
- Polypropylene (unspecified)
- Fillers Included
- Glass Fiber
- Processing Methods
- Injection Molding
- Note
¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design. ² Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article. ³ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Industrial
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Chemically Coupled
- Heat Stabilized
- High Stiffness
- High Strength
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Automotive Applications
- Commercial Appliance
- Construction Applications
- Home Appliances
- Water Management
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break, 5 mm/min) ¹ | 120.0 | MPa | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹ | 1.2 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹ | 15100.0 | MPa | ISO 527 |
| Flexural Modulus (at 2 mm/min) ¹ | 13700.0 | MPa | ISO 178 |
| Flexural Stress (Break, 2 mm/min) ¹ | 175.0 | MPa | ISO 178 |
| Tensile Modulus (at 5 mm/min) ¹ | 17300.0 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹ | 1.1 | % | ASTM D638 |
| Tensile Stress (Break, Type I, 5 mm/min) ¹ | 120.0 | MPa | ASTM D638 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹ | 13800.0 | MPa | ASTM D790 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹ | 170.0 | MPa | ASTM D790 |
| Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹ | 135.0 | MPa | ASTM D790 |
Table 2 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹ | 1.47 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) ¹ | 0.04 | % | ISO 62 |
| Mold Shrinkage (flow, 24 hrs) ² | 0.6 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ² | 0.8 | % | ASTM D955 |
Table 3 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature/Af (1.8 MPa Flatw 80*10*4 sp=64mm) ¹ | 154.0 | °C | ISO 75/Af |
| Heat Deflection Temperature/Bf (0.45 MPa Flatw 80*10*4 sp=64mm) ¹ | 160.0 | °C | ISO 75/Bf |
| Heat Deflection Temperature (1.82 MPa, 3.2mm, unannealed) ¹ | 156.0 | °C | ASTM D648 |
Table 4 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched 80*10*4 +23°C) ¹ | 14.0 | kJ/m² | ISO 180/1A |
| Izod Impact (Unnotched 80*10*4 +23°C) ¹ | 39.0 | kJ/m² | ISO 180/1U |
| Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹ | 13.0 | kJ/m² | ISO 179/1eA |
| Charpy Impact (at 23°C, Unnotch Edgew 80*10*4 sp=62mm) ¹ | 29.0 | kJ/m² | ISO 179/1eU |
| Izod Impact (Notched, 23°C) ¹ | 155.0 | J/m | ASTM D256 |
| Izod Impact (Unnotched, 23°C) ¹ | 620.0 | J/m | ASTM D4812 |
Table 5 of 5
9 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ³ | 80.0 | °C |
| Drying Time ³ | 4.0 | Hrs |
| Melt Temperature ³ | 220 - 250 | °C |
| Front - Zone 3 Temperature ³ | 250 - 260 | °C |
| Middle - Zone 2 Temperature ³ | 245 - 255 | °C |
| Rear - Zone 1 Temperature ³ | 230 - 245 | °C |
| Mold Temperature ³ | 40 - 65 | °C |
| Back Pressure ³ | 0.2 - 0.3 | MPa |
| Screw Speed ³ | 30 - 60 | rpm |