LNP™ THERMOCOMP™ AM Compound EZ006EXAR1

Chemical Family: Polyetherimide (PEI)Polyimides (PI)

SABIC's Specialties Business LNP™ THERMOCOMP™ EZ006EXAR1is a compound based on Polyetherimide (PEI) resin containing 30% milled glass fiber for Large Format Additive manufacturing (LFAM) applications requiring better dimensional stability and low thermal expansion. PEI compounds, based on SABIC's inherently flame-retardant ULTEM™ resins, offer high temperature performance, excellent strength-to-weight ratio, high modulus and low creep.

Product families

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Other characteristics

Brand: LNP™ THERMOCOMP™ AM Compound
Density: 1510.0 - 1510.0 kg/m³
Polymer Name: Polyether Imide (PEI)
Fillers Included: Glass Fiber, Milled Glass Fiber
Glass Fiber
Milled Glass Fiber
Additives Included: Flame Retardant
Processing Methods: 3D Printing, Fused Filament Fabrication, Fused Granulate Fabrication (FGF), Large Format Additive Manufacturing (LFAM)
Note: ⁿ Tensile Stiffness (K) is a structural property defined as the stress/strain in the linear region of the stress/strain curve. Value depends on the geometry/shape and boundary/surrounding conditions.
Markets: Industrial
Technology: Plastics
Material Features: Cost Effective
Creep Resistant
Dimensional Stability
Flame Retardant
Good Mechanical Properties
High Modulus
High Stiffness
High Strength to Weight Ratio
Country Availability: Canada
China (Mainland)
Mexico
USA
Plastics and Elastomers End Uses: 3D Printing Applications
Industrial Applications
Industrial Parts
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: 3D Printing
Fused Filament Fabrication
Fused Granulate Fabrication (FGF)
Large Format Additive Manufacturing (LFAM)

Technical data

Table 1 of 4

8 rows

Characteristic	Value	Unit	Method
Tensile Stress (at 5mm/min, XZ Orientation)	84	MPa	ASTM D638 Modified
Tensile Stress (at 5mm/min, ZX Orientation)	45	MPa	ASTM D638 Modified
Tensile Strain (at 5mm/min, XZ Orientation)	2.4	%	ASTM D638 Modified
Tensile Strain (at 5mm/min, ZX Orientation)	1.5	%	ASTM D638 Modified
Tensile Stiffness (at 5mm/min, XZ Orientation) ⁿ	5.8	GPa	ASTM D638 Modified
Tensile Stiffness (at 5mm/min, ZX Orientation)	3.5	GPa	ASTM D638 Modified
Flexural Stress (at 5mm/min, XZ Orientation)	67	MPa	ASTM D790 Modified
Flexural Stress (at 5mm/min, ZX Orientation)	131	MPa	ASTM D790 Modified

Table 2 of 4

1 row

Characteristic	Value	Method
Specific Gravity	1.51	ASTM D792

Table 3 of 4