LNP™ THERMOCOMP™ AM Compound EC004EXAR1

Chemical Family: Polyetherimide (PEI)Polyimides (PI)

SABIC's Specialties Business LNP™ THERMOCOMP™ EC004EXAR1 compound is based on Polyetherimide (PEI) resin containing 20% carbon fiber designed to provide a Wider Process Window and Easier Flow for Large Format Additive Manufacturing (LFAM) applications needing High heat performance. PEI compounds, based on SABIC's inherently flame-retardant ULTEM™ resins, provide Low Thermal Expansion, High Temperature Performance, Excellent Strength-to-Weight Ratio, High Modulus and Low Creep.

Product families

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Other characteristics

Brand: LNP™ THERMOCOMP™ AM Compound
Density: 1340.0 - 1340.0 kg/m³
Polymer Name: Polyether Imide (PEI)
Fillers Included: Carbon Fiber
Additives Included: Flame Retardant
Processing Methods: 3D Printing, Fused Filament Fabrication, Fused Granulate Fabrication (FGF), Large Format Additive Manufacturing (LFAM)
Note: ⁿ Tensile Stiffness (K) is a structural property defined as the stress/strain in the linear region of the stress/strain curve. Value depends on the geometry/shape and boundary/surrounding conditions.
Markets: Industrial
Technology: Plastics
Material Features: Broad Processing Window
Cost Effective
Creep Resistant
Dimensional Stability
Flame Retardant
Good Flow
Heat Resistance
High Modulus
Country Availability: Canada
China (Mainland)
Mexico
USA
Plastics and Elastomers End Uses: 3D Printing Applications
Industrial Applications
Industrial Parts
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: 3D Printing
Fused Filament Fabrication
Fused Granulate Fabrication (FGF)
Large Format Additive Manufacturing (LFAM)

Technical data

Table 1 of 4

8 rows

Characteristic	Value	Unit	Method
Tensile Stress (at 5mm/min, XZ Orientation)	159	MPa	ASTM D638 Modified
Tensile Stress (at 5mm/min, ZX Orientation)	54	MPa	ASTM D638 Modified
Tensile Strain (at 5mm/min, XZ Orientation)	1.4	%	ASTM D638 Modified
Tensile Strain (at 5mm/min, ZX Orientation)	1.6	%	ASTM D638 Modified
Tensile Stiffness (at 5mm/min, XZ Orientation) ⁿ	13.8	GPa	ASTM D638 Modified
Tensile Stiffness (at 5mm/min, ZX Orientation)	3.8	GPa	ASTM D638 Modified
Flexural Stress (at 5mm/min, XZ Orientation)	69	MPa	ASTM D790 Modified
Flexural Stress (at 5mm/min, ZX Orientation)	217	MPa	ASTM D790 Modified

Table 2 of 4

1 row

Characteristic	Value	Method
Specific Gravity	1.34	ASTM D792

Table 3 of 4