LNP™ LUBRICOMP™ Compound RCL36
- Chemical Family
- Polyamides
SABIC's Specialties Business LNP LUBRICOMP RCL36 compound is based on Nylon 6/6 resin containing 15% PTFE, 30% carbon fiber. Added features of this grade include: Wear Resistant, Electrically Conductive.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Lawn & Garden
- Consumer Goods — Sports & Recreation
- Artificial Turf
- Consumer Electronics
- Displays
- Non-Food Consumer Packaging
- Applicators & Accessories
- Connectors
- Switches & Relays
Product Families
- Polyamides
Other characteristics
- Brand
- LNP™ LUBRICOMP™ Compound
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- Carbon Fiber, PTFE
- Carbon Fiber
- PTFE
- Flexural Modulus
- 18400.0 - 18400.0 MPa
- Additives Included
- Lubricant (PTFE), Mold Release Agent
- Lubricant (PTFE)
- Mold Release Agent
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Material Features
- Electrically Conductive
- Friction Resistant
- Good Mold Release
- High Stiffness
- High Strength
- Light Weight
- Wear Resistant
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Building Materials
- Cell Phones
- Circuit Protection
- Commercial Appliance
- Computer Components
- Consumer Applications
- Containers
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break) ¹¹ | 182 | MPa | ASTM D638 |
| Tensile Stress (Break) ¹¹ | 245 | MPa | ISO 527 |
| Tensile Stress (Yield, 5 mm/min) ¹¹ | 220 | MPa | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 1.6 | % | ISO 527 |
| Tensile Strain (Break) ¹¹ | 0.9 | % | ASTM D638 |
| Tensile Strain (Break) ¹¹ | 1.8 | % | ISO 527 |
| Flexural Stress (Yield, at 2 mm/min) ¹¹ | 315 | MPa | ISO 178 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 32400 | MPa | ASTM D638 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 16800 | MPa | ISO 178 |
| Flexural Stress ¹¹ | 372 | MPa | ASTM D790 |
| Flexural Stress ¹¹ | 396 | MPa | ISO 178 |
| Flexural Modulus ¹¹ | 18400 | MPa | ASTM D790 |
Table 2 of 7
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Wear Factor Washer ¹¹ | 15 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic COF ¹¹ | 0.36 | — | ASTM D3702 Modified: Manual |
| Density ¹¹ | 1.38 | g/cm³ | ISO 1183 |
| Density ¹¹ | 1.37 | g/cm³ | ASTM D792 |
| Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.5 | % | ASTM D570 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.1 | % | ASTM D955 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.11 | % | ISO 294 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.7 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.72 | % | ISO 294 |
| Static COF ¹¹ | 0.3 | — | ASTM D3702 Modified: Manual |
Table 3 of 7
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.000005 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ | 0.00008 | 1/°C | ISO 11359-2 |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | min. 240 | °C | ISO 75/Af |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 251 | °C | ISO 75/Af |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 65 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 65 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 65 | °C | UL 746B |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 255 | °C | ASTM D648 |
Table 4 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Surface Resistivity ¹¹ | 10 - 1000 | Ω | ASTM D257 |
Table 5 of 7
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 64 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 10 | kJ/m² | ISO 180/1A |
| Izod Impact (Unnotched, at 23°C) ¹¹ | 1068 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 101 | J/m | ASTM D256 |
| Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹ | 10 | J | ASTM D3763 |
| Multi-Axial Impact ¹¹ | 4 | J | ISO 6603 |
Table 6 of 7
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.15 - 0.25 | % |
| Melt Temperature ⁷ | 280 - 305 | °C |
| Front - Zone 3 Temperature ⁷ | 295 - 305 | °C |
| Middle - Zone 2 Temperature ⁷ | 280 - 295 | °C |
| Rear - Zone 1 Temperature ⁷ | 265 - 275 | °C |
| Mold Temperature ⁷ | 95 - 110 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |
Table 7 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94HB Flame Class Rating) ᵖ | 1.5 | mm | UL 94 |