LNP™ KONDUIT™ Compound PX10323
- Chemical Family
- Polyamides
SABIC's Specialties Business LNP KONDUIT PX10323 compound is based on Nylon 6 resin containing glass fiber and proprietary thermal filler. Added features of this grade include: Thermally Conductive. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Automotive Lighting
- Glazing & Window Elements
- Interior Fixtures
- Equipment & Parts
- Automotive Electronics
- Consumer Electronics
- Displays
- Industrial Automation
- Lighting
Product Families
- Polyamides
Other characteristics
- Brand
- LNP™ KONDUIT™ Compound
- Polymer Name
- Polyamide 6 (PA 6)
- Fillers Included
- Glass Fiber, Graphite, Proprietary
- Glass Fiber
- Graphite
- Proprietary
- Flexural Modulus
- 14300.0 - 14300.0 MPa
- Additives Included
- Heat Stabilizer, Mold Release Agent
- Heat Stabilizer
- Mold Release Agent
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Industrial
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Good Mold Release
- Heat Stabilized
- No Added PFAS
- Thermally Conductive
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Automotive Electronics
- Building Materials
- Cell Phones
- Computer Components
- Construction Applications
- Consumer Applications
- Displays
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 70 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 0.9 | % | ASTM D638 |
| Tensile Modulus (at 5 mm/min) ¹¹ | 13700 | MPa | ASTM D638 |
| Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹ | 95 | MPa | ASTM D790 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 96 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 14200 | MPa | ASTM D790 |
| Tensile Stress (Break, 5 mm/min) ¹¹ | 73 | MPa | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 0.8 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 14000 | MPa | ISO 527 |
| Flexural Stress (Break, 2 mm/min) ¹¹ | 96 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 14300 | MPa | ISO 178 |
| Impact Strength ¹¹ | 3.7 - 6.8 | kJ/m² | ISO R179 |
Table 2 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.61 | g/cm³ | ASTM D792 |
| Density ¹¹ | 1.61 | g/cm³ | ISO 1183 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.2 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.22 | % | ASTM D955 |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.04 | % | ISO 62 |
Table 3 of 7
18 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 186 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.0000161 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.0000356 | 1/°C | ASTM E831 |
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 204 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at 40°C to 120°C, flow) ¹¹ | 0.0000124 | 1/°C | ASTM E831 |
| Thermal Conductivity (in-plane, 25*0.4mm disc) ¹¹ | 15 | W/m-K | ASTM E1461-07 |
| Coefficient of Thermal Expansion (at 40°C to 120°C, xflow) ¹¹ | 0.0000727 | 1/°C | ASTM E831 |
| Thermal Conductivity (through-plane, 10*10*3mm sample) ¹¹ | 3.5 | W/m-K | ASTM E1461-07 |
| Thermal Conductivity (in-plane, 60*60*3mm plaque) ¹¹ | 18 | W/m-K | ISO 22007-2 |
| Thermal Conductivity (through-plane, 60*60*3mm plaque) ¹¹ | 1.5 | W/m-K | ISO 22007-2 |
| Coefficient of Thermal Expansion (at -30°C to 80°C, flow) ¹¹ | 0.000014 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -30°C to 80°C, xflow) ¹¹ | 0.0000395 | 1/°C | ISO 11359-2 |
Table 4 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Surface Resistivity ¹¹ | 1050000 | Ω | ASTM D257 |
Table 5 of 7
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, at 23°C) ¹¹ | 73 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 30 | J/m | ASTM D256 |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 6 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 3 | kJ/m² | ISO 180/1A |
Table 6 of 7
20 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 - 90 | °C |
| Drying Temperature ⁷ | 80 | °C |
| Drying Time ⁷ | 3 - 4 | Hrs |
| Drying Time ⁷ | 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.15 - 0.25 | % |
| Melt Temperature ⁷ | 270 - 300 | °C |
| Melt Temperature ⁷ | 270 - 295 | °C |
| Nozzle Temperature ⁷ | 270 - 300 | °C |
| Front - Zone 3 Temperature ⁷ | 270 - 290 | °C |
| Front - Zone 3 Temperature ⁷ | 270 - 300 | °C |
| Middle - Zone 2 Temperature ⁷ | 270 - 290 | °C |
| Middle - Zone 2 Temperature ⁷ | 270 - 300 | °C |
Table 7 of 7
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94HB Flame Class Rating) ᵖ | min. 0.75 | mm | UL 94 |
| Glow Wire Flammability Index (at 1 mm) ᵖ | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index (at 1.5 mm) ᵖ | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index (at 3 mm) ᵖ | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignitability Temperature (at 1.0 mm) ᵖ | 825 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature (at 1.5 mm) ᵖ | 850 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature (at 3.0 mm) ᵖ | 960 | °C | IEC 60695-2-13 |
| Glow Wire Flammability Index (passes at 850°C) ᵖ | 1 | mm | IEC 60695-2-12 |
| Glow Wire Flammability Index (passes at 960°C) ᵖ | 1.6 | mm | IEC 60695-2-12 |