LNP™ THERMOCOMP™ AM Compound JC004XXAR1

Chemical Family: Polysulfones

SABIC's Specialties Business LNP THERMOCOMP AM JC004XXAR1 is a compound based on PESU (Polyethersulfone) resin containing 20% carbon fiber for Large Format Additive manufacturing (LFAM) applications needing an inherent FR, reinforcement, and a high heat amorphous solution. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.

Product families

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Other characteristics

Brand: LNP™ THERMOCOMP™ AM Compound
Density: 1430.0 - 1430.0 kg/m³
Polymer Name: Polyethersulfone (PES)
Fillers Included: Carbon Fiber
Additives Included: Flame Retardant
Processing Methods: 3D Printing, Fused Filament Fabrication, Fused Granulate Fabrication (FGF), Large Format Additive Manufacturing (LFAM)
Note: ⁿ Tensile Stiffness (K) is a structural property defined as the stress/strain in the linear region of the stress/strain curve. Value depends on the geometry/shape and boundary/surrounding conditions.
Markets: Industrial
Technology: Plastics
Labeling Claims: No Added PFAS
Material Features: Amorphous
Cost Effective
Flame Retardant
Heat Resistance
No Added PFAS
Very Good Heat Resistance
Country Availability: Canada
China (Mainland)
Mexico
USA
Plastics and Elastomers End Uses: 3D Printing Applications
Industrial Applications
Industrial Parts
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: 3D Printing
Fused Filament Fabrication
Fused Granulate Fabrication (FGF)
Large Format Additive Manufacturing (LFAM)

Technical data

Table 1 of 4

8 rows

Characteristic	Value	Unit	Method
Tensile Stress (at 5mm/min, XZ Orientation)	84	MPa	ASTM D638 Modified
Tensile Stress (at 5mm/min, ZX Orientation)	23	MPa	ASTM D638 Modified
Tensile Strain (at 5mm/min, XZ Orientation)	1.4	%	ASTM D638 Modified
Tensile Strain (at 5mm/min, ZX Orientation)	1.2	%	ASTM D638 Modified
Tensile Stiffness (at 5mm/min, XZ Orientation) ⁿ	7.8	GPa	ASTM D638 Modified
Tensile Stiffness (at 5mm/min, ZX Orientation)	2.2	GPa	ASTM D638 Modified
Flexural Stress (at 5mm/min, XZ Orientation)	37	MPa	ASTM D790 Modified
Flexural Stress (at 5mm/min, ZX Orientation)	103	MPa	ASTM D790 Modified

Table 2 of 4

1 row

Characteristic	Value	Method
Specific Gravity	1.43	ASTM D792

Table 3 of 4