LNP™ LUBRICOMP™ Compound DL0029E
- Chemical Family
- Polycarbonate (PC)
LNP LUBRICOMP DL0029E compound is based on Polycarbonate (PC) resin containing 10% PTFE. Added features of this grade include: Wear Resistant, Flame Retardant.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Lawn & Garden
- Consumer Goods — Sports & Recreation
- Artificial Turf
- Consumer Electronics
- Displays
- Non-Food Consumer Packaging
- Applicators & Accessories
- Connectors
- Switches & Relays
Product Families
- High Performance Thermoplastics
- Polycarbonates
Other characteristics
- Brand
- LNP™ LUBRICOMP™ Compound
- Polymer Name
- Polycarbonate (PC)
- Fillers Included
- PTFE
- Additives Included
Flame Retardant, Heat Stabilizer, Lubricant (PTFE), Mold Release Agent; Flame Retardant; Heat Stabilizer; Lubricant (PTFE); Mold Release Agent
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Flame Rating
- UL 94 V0
- Technology
- Plastics
- Material Features
- Flame Retardant
- Friction Resistant
- Good Mold Release
- Good Moldability
- Heat Stabilized
- UL Listed
- Unreinforced
- Wear Resistant
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Building Materials
- Cash Dispenser (ATM)
- Cell Phones
- Commercial Appliance
- Computer Components
- Consumer Applications
- Containers
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
19 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, 5 mm/min) ¹¹ | 56 | MPa | ISO 527 |
| Tensile Strain (Yield, 5 mm/min) ¹¹ | 5.1 | % | ISO 527 |
| Tensile Stress (Yield, Type I, 5 mm/min) ¹¹ | 56 | MPa | ASTM D638 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 2400 | MPa | ISO 527 |
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 47 | MPa | ASTM D638 |
| Flexural Stress (Yield, at 2 mm/min) ¹¹ | 82 | MPa | ISO 178 |
| Flexural Strain (Break, at 2 mm/min) ¹¹ | 7 | % | ISO 178 |
| Tensile Strain (Yield, Type I, 5 mm/min) ¹¹ | 5.7 | % | ASTM D638 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 2700 | MPa | ISO 178 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 33 | % | ASTM D638 |
| Flexural Strain (Break, at 2 mm/min, 60°C) ¹¹ | 7 | % | ISO 178 |
| Tensile Modulus (at 5 mm/min) ¹¹ | 2240 | MPa | ASTM D638 |
Table 2 of 6
13 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.31 | — | ASTM D792 |
| Density ¹¹ | 1.27 | g/cm³ | ISO 1183 |
| Density ¹¹ | 1.31 | g/cm³ | ASTM D792 |
| Mold Shrinkage (on Tensile Bar, flow) ᵍ ¹¹ | 0.7 - 0.9 | % | SABIC method |
| Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.01 | % | ASTM D570 |
| Wear Factor Washer ¹¹ | 16 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Wear Factor Washer ¹¹ | 55 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic COF ¹¹ | 0.32 | — | ASTM D3702 Modified: Manual |
| Dynamic COF ¹¹ | 0.2 | — | ASTM D3702 Modified: Manual |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.6 - 0.8 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.8 - 1 | % | ASTM D955 |
| Melt Volume Rate (at 275°C, 2.16 kg) ¹¹ | 24 - 32 | cm³/10 min | ISO 1133 |
Table 3 of 6
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 141 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.00009 | 1/°C | ISO 11359-2 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 130 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -30°C to 30°C, flow) ¹¹ | 0.000071 | 1/°C | ASTM D696 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ | 0.000088 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -30°C to 30°C, xflow) ¹¹ | 0.000075 | 1/°C | ASTM D696 |
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 139 | °C | ISO 75/Bf |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 128 | °C | ISO 75/Af |
Table 4 of 6
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, at 23°C) ¹¹ | 2020 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 119 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 46 | J | ASTM D3763 |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 135 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 6 | kJ/m² | ISO 180/1A |
Table 5 of 6
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 120 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 300 - 315 | °C |
| Front - Zone 3 Temperature ⁷ | 310 - 320 | °C |
| Middle - Zone 2 Temperature ⁷ | 305 - 315 | °C |
| Rear - Zone 1 Temperature ⁷ | 295 - 305 | °C |
| Mold Temperature ⁷ | 80 - 110 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |
Table 6 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94V-0 Flame Class Rating) ᵖ | min. 1.7 | mm | UL 94 |