LNP™ LUBRICOMP™ Compound UFL269SA

Chemical Family: Polyamides

SABIC's Specialties Business LNP LUBRICOMP UFL269SA compound is based on Polyphthalamide (PPA) resin containing 30% glass fiber, 10% PTFE. Added features of this grade include: Wear Resistant, Heat Stabilized, Flame Retardant.

Product families

Applications

Consumer Goods — Appliances & Electronics

Automotive & Transportation — Automotive

Powertrain & UTH

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Electrical & Electronics — Devices & Assemblies

Consumer Electronics
Displays

Electrical & Electronics — Parts & Components

Semiconductor Manufacturing

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Other characteristics

Brand: LNP™ LUBRICOMP™ Compound
Polymer Name: Polyphthalamide (PPA)
Fillers Included: Glass Fiber, PTFE
Glass Fiber
PTFE
Flexural Modulus: 12820.0 - 12820.0 MPa
Additives Included: Flame Retardant, Heat Stabilizer, Lubricant (PTFE), Mold Release Agent; Flame Retardant; Heat Stabilizer; Lubricant (PTFE); Mold Release Agent
Processing Methods: Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
Markets: Automotive & Transportation
Consumer Goods
Electrical & Electronics
Industrial
Flame Rating: UL 94 V0
Technology: Plastics
Material Features: Flame Retardant
Friction Resistant
Good Mold Release
Heat Stabilized
High Stiffness
High Temperature Resistance
Very Good Heat Resistance
Wear Resistant
Certifications and Compliance: UL 94
Plastics and Elastomers End Uses: Appliances
Automotive Applications
Automotive Under The Hood
Cell Phones
Commercial Appliance
Computer Components
Consumer Applications
Displays
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 6

5 rows

Characteristic	Value	Unit	Method
Tensile Stress (Break) ¹¹	162	MPa	ASTM D638
Tensile Strain (Break) ¹¹	1.7	%	ASTM D638
Tensile Modulus (at 50 mm/min) ¹¹	13650	MPa	ASTM D638
Flexural Stress ¹¹	227	MPa	ASTM D790
Flexural Modulus ¹¹	12820	MPa	ASTM D790

Table 2 of 6

6 rows

Characteristic	Value	Unit	Method
Density ¹¹	1.71	g/cm³	ASTM D792
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.2 - 0.4	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	0.7 - 0.9	%	ASTM D955
Wear Factor Washer ¹¹	85	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF ¹¹	0.47	—	ASTM D3702 Modified: Manual
Static COF ¹¹	0.38	—	ASTM D3702 Modified: Manual

Table 3 of 6

1 row

Characteristic	Value	Unit	Method
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	273	°C	ASTM D648

Table 4 of 6

2 rows

Characteristic	Value	Unit	Method
Izod Impact (Unnotched, at 23°C) ¹¹	461	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	85	J/m	ASTM D256

Table 5 of 6

10 rows

Characteristic	Value	Unit
Drying Temperature ⁷	120	°C
Drying Time ⁷	4	Hrs
Maximum Moisture Content ⁷	0.15	%
Melt Temperature ⁷	315 - 330	°C
Front - Zone 3 Temperature ⁷	325 - 340	°C
Middle - Zone 2 Temperature ⁷	315 - 325	°C
Rear - Zone 1 Temperature ⁷	310 - 320	°C
Mold Temperature ⁷	150 - 170	°C
Back Pressure ⁷	0.2 - 0.3	MPa
Screw Speed ⁷	30 - 60	rpm

Table 6 of 6