LNP™ KONDUIT™ Compound PX11311U
- Chemical Family
- Polyamides
SABIC's Specialties Business LNP KONDUIT PX11311U compound is based on Nylon 6 resin containing mineral and glass fiber. Added features of this grade include: Thermally Conductive, Electrically Insulative, Improved UV Stability and Non-Brominated, Non-Chlorinated Flame Retardant.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Automotive Lighting
- Glazing & Window Elements
- Interior Fixtures
- Equipment & Parts
- Automotive Electronics
- Consumer Electronics
- Displays
- Industrial Automation
- Lighting
- Housings & Enclosures
Product Families
- Polyamides
Other characteristics
- Brand
- LNP™ KONDUIT™ Compound
- Polymer Name
- Polyamide 6 (PA 6)
- Fillers Included
- Glass Fiber, Mineral, Silicone, Silicone Oil
- Glass Fiber
- Mineral
- Silicone
- Silicone Oil
- Flexural Modulus
- 11000.0 - 11000.0 MPa
- Additives Included
- Flame Retardant, Heat Stabilizer, UV Stabilizer
- Flame Retardant
- Heat Stabilizer
- UV Stabilizer
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Industrial
- Flame Rating
- UL 94 V0
- Technology
- Plastics
- Labeling Claims
- Bromine-free
- Chlorine-free
- Material Features
- Electrically Insulating
- Electrically Isolative
- Flame Retardant
- Good Heat Dissipation
- Good UV Resistance
- Good UV Stability
- Good Weather Stability
- Heat Stabilized
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Automotive Electronics
- Building Materials
- Camera Applications
- Cell Phones
- Computer Components
- Construction Applications
- Cooling Fan
- Displays
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break, 5 mm/min) ¹¹ | 105 | MPa | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 1.7 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 12000 | MPa | ISO 527 |
| Flexural Stress (Yield, at 2 mm/min) ¹¹ | 170 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 1.10E+04 | MPa | ISO 178 |
Table 2 of 7
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.45 | % | ISO 294 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.65 | % | ISO 294 |
| Density ¹¹ | 1.74 | g/cm³ | ISO 1183 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.36 | % | ISO 62-1 |
Table 3 of 7
19 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm) ¹¹ | 209 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.0000308 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.0000477 | 1/°C | ASTM E831 |
| Thermal Conductivity (through-plane, 60*60*3mm plaque) ¹¹ | 0.8 | W/m-K | ISO 22007-2 |
| Thermal Conductivity (in-plane, 60*60*3mm plaque) ¹¹ | 1.5 | W/m-K | ISO 22007-2 |
| Coefficient of Thermal Expansion (at -30°C to 80°C, flow) ¹¹ | 0.0000346 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -30°C to 80°C, xflow) ¹¹ | 0.0000604 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 80°C, flow) ¹¹ | 0.0000372 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 80°C, xflow) ¹¹ | 0.0000734 | 1/°C | ISO 11359-2 |
| Thermal Conductivity (through-plane, 80*3mm disc) ¹¹ | 1.1 | W/m-K | ISO 22007-2 |
| Thermal Conductivity (in-plane, 80*3mm disc) ¹¹ | 1.3 | W/m-K | ISO 22007-2 |
| Ball Pressure Test (at 123°C to 127°C) ¹¹ | Pass | — | IEC 60695-10-2 |
Table 4 of 7
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Surface Resistivity ¹¹ | 1.00E+16 | Ω | ASTM D257 |
| Dielectric Strength (in oil, at 1.6mm) ¹¹ | 15.9 | kV/mm | ASTM D149 |
| Comparative Tracking Index (UL, PLC) ¹¹ | 0 | PLC Code | UL 746A |
| Comparative Tracking Index ʳ ¹¹ | 600 | V | IEC 60112 |
| Hot Wire Ignition (PLC 0) ¹¹ | min. 1 | mm | UL 746A |
| High Ampere Arc Ignition (PLC 0) ¹¹ | min. 1 | mm | UL 746A |
Table 5 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 25 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 3 | kJ/m² | ISO 180/1A |
Table 6 of 7
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.15 - 0.25 | % |
| Melt Temperature ⁷ | 270 - 295 | °C |
| Front - Zone 3 Temperature ⁷ | 270 - 290 | °C |
| Middle - Zone 2 Temperature ⁷ | 270 - 290 | °C |
| Rear - Zone 1 Temperature ⁷ | 260 - 275 | °C |
| Mold Temperature ⁷ | 85 - 100 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 20 - 60 | rpm |
Table 7 of 7
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94V-0 Flame Class Rating) ᵖ | min. 1 | mm | UL 94 |
| Glow Wire Ignitability Temperature (at 1.0 mm) ᵖ | 800 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature (at 1.5 mm) ᵖ | 775 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature (at 1.6 mm) ᵖ | 775 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature (at 3.0 mm) ᵖ | 800 | °C | IEC 60695-2-13 |
| Glow Wire Flammability Index (at 3 mm) ᵖ | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index (at 1.5 mm) ᵖ | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index (at 1 mm) ᵖ | 960 | °C | IEC 60695-2-12 |