LNP™ COLORCOMP™ Compound D1000F
- Chemical Family
- Polycarbonate (PC)
SABIC's Specialties Business LNP COLORCOMP D1000F compound is based on unfilled Polycarbonate (PC) resin. Added features of this grade include: Superior Molding. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Housewares
- Consumer Goods — Sports & Recreation
- Interior
- Consumer Electronics
- Displays
- Non-Food Consumer Packaging
- Applicators & Accessories
Product Families
- High Performance Thermoplastics
- Polycarbonates
Other characteristics
- Brand
- LNP™ COLORCOMP™ Compound
- Polymer Name
- Polycarbonate (PC)
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Color
- Custom
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Excellent Aesthetics
- Good Aesthetics
- Good Moldability
- Good Processability
- Good Surface Appearance
- Heat Stabilized
- High Durability
- No Added PFAS
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Automotive Applications
- Automotive Interior Parts
- Cell Phones
- Commercial Appliance
- Computer Components
- Consumer Applications
- Containers
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 8
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.19 | g/cm³ | ASTM D792 |
| Melt Flow Rate (at 300°C, 1.2 kgf) ¹¹ | 17.5 | g/10 min | ASTM D1238 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.5 - 0.7 | % | SABIC method |
| Specific Gravity ¹¹ | 1.2 | — | ASTM D792 |
| Specific Volume ¹¹ | 0.83 | cm³/g | ASTM D792 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.15 | % | ASTM D570 |
| Water Absorption (at 23°C, saturated) ¹¹ | 0.35 | % | ASTM D570 |
| Water Absorption (Equilibrium, at 100°C) ¹¹ | 0.58 | % | ASTM D570 |
Table 2 of 8
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2340 | MPa | ASTM D790 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 96 | MPa | ASTM D790 |
| Hardness (Rockwell M) ¹¹ | 70 | — | ASTM D785 |
| Hardness (Rockwell R) ¹¹ | 118 | — | ASTM D785 |
| Taber Abrasion (CS-17, 1 kg) ¹¹ | 10 | mg/1000cy | ASTM D1044 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 125 | % | ASTM D638 |
| Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ | 7 | % | ASTM D638 |
| Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 68 | MPa | ASTM D638 |
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 62 | MPa | ASTM D638 |
Table 3 of 8
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Thermal Expansion (at -40°C to 95°C, flow) ¹¹ | 0.0000684 | 1/°C | ASTM E831 |
| Heat Deflection Temperature (at 0.45 MPa, 6.4 mm, Unannealed) ¹¹ | 137 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 129 | °C | ASTM D648 |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 130 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 130 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 130 | °C | UL 746B |
| Specific Heat ¹¹ | 1.25 | J/g-°C | ASTM C351 |
| Thermal Conductivity ¹¹ | 0.25 | W/m-°C | ASTM C177 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 154 | °C | ASTM D1525 |
Table 4 of 8
13 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Comparative Tracking Index (UL, PLC) ¹¹ | 2 | PLC Code | UL 746A |
| Dielectric Strength (in air, at 3.2mm) ¹¹ | 14.9 | kV/mm | ASTM D149 |
| Dissipation Factor (at 50/60 Hz) ¹¹ | 0.0009 | — | ASTM D150 |
| Dissipation Factor (at at 1 MHz) ¹¹ | 0.01 | — | ASTM D150 |
| High Ampere Arc Ignition (PLC 0) ¹¹ | min. 1.5 | mm | UL 746A |
| High Ampere Arc Ignition (PLC 1) ¹¹ | min. 3 | mm | UL 746A |
| High Ampere Arc Ignition (PLC 2) ¹¹ | min. 1.1 | mm | UL 746A |
| High Voltage Arc Track Rate (PLC) ¹¹ | 2 | PLC Code | UL 746A |
| Hot Wire Ignition (PLC 2) ¹¹ | min. 1.5 | mm | UL 746A |
| Hot Wire Ignition (PLC 3) ¹¹ | min. 1.1 | mm | UL 746A |
| Relative Permittivity (1 MHz) ¹¹ | 2.96 | — | ASTM D150 |
| Relative Permittivity (50/60 Hz) ¹¹ | 3.17 | — | ASTM D150 |
Table 5 of 8
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Haze (at 2.54 mm) ¹¹ | 1 | % | ASTM D1003 |
| Light Transmission (at 2.54 mm) ¹¹ | 88 | % | ASTM D1003 |
| Refractive Index ¹¹ | 1.586 | — | ASTM D542 |
Table 6 of 8
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Falling Dart Impact (at 23°C) ¹¹ | 169 | J | ASTM D3029 |
| Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹ | 62 | J | ASTM D3763 |
| Izod Impact (Notched, at 23°C) ¹¹ | 694 | J/m | ASTM D256 |
| Izod Impact (Unnotched, at 23°C) ¹¹ | 3204 | J/m | ASTM D4812 |
| Tensile Impact Strength (Type S) ¹¹ | 546 | kJ/m² | ASTM D1822 |
Table 7 of 8
14 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 120 | °C |
| Drying Time ⁷ | 3 - 4 | Hrs |
| Drying Time (Cumulative) ⁷ | 48 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 280 - 305 | °C |
| Nozzle Temperature ⁷ | 275 - 300 | °C |
| Front - Zone 3 Temperature ⁷ | 280 - 305 | °C |
| Middle - Zone 2 Temperature ⁷ | 270 - 295 | °C |
| Rear - Zone 1 Temperature ⁷ | 260 - 280 | °C |
| Mold Temperature ⁷ | 70 - 95 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed ⁷ | 40 - 70 | rpm |
Table 8 of 8
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94HB Flame Class Rating) ᵖ | min. 0.7 | mm | UL 94 |
| UV-light (Water exposure/immersion) ᵖ | F2 | — | UL 746C |