LNP™ LUBRICOMP™ Compound IFL36R
- Chemical Family
- Polyamides
SABIC's Specialties Business LNP LUBRICOMP IFL36R compound is based on Nylon 6/12 resin containing 30% glass fiber, 15% PTFE. Added features of this grade include: Wear Resistant, Mold Release.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Lawn & Garden
- Consumer Goods — Sports & Recreation
- Artificial Turf
- Consumer Electronics
- Displays
- Non-Food Consumer Packaging
- Applicators & Accessories
- Connectors
- Switches & Relays
Product Families
- Polyamides
Other characteristics
- Brand
- LNP™ LUBRICOMP™ Compound
- Polymer Name
- Polyamide 612 (PA 612)
- Fillers Included
- Glass Fiber, PTFE
- Glass Fiber
- PTFE
- Flexural Modulus
- 7300.0 - 7300.0 MPa
- Additives Included
Heat Stabilizer, Lubricant (PTFE), Mold Release Agent; Heat Stabilizer; Lubricant (PTFE); Mold Release Agent
- Processing Methods
- Injection Molding
- Note
⁷ Параметры литья под давлением упоминаются только в качестве общих рекомендаций. Они могут не применяться или требовать корректировки в конкретных ситуациях, таких как малые размеры литья, литье крупных деталей, литье тонкостенных изделий и газовое литье.. ¹¹ Информация, указанная в технических паспортах, должна использоваться только в качестве ориентировочной для целей выбора материала и не должна использоваться в качестве спецификации или для проектирования деталей или пресс-форм.
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Technology
- Plastics
- Material Features
- Friction Resistant
- Good Mold Release
- Heat Stabilized
- High Stiffness
- Wear Resistant
- Plastics and Elastomers End Uses
- Appliances
- Building Materials
- Cash Dispenser (ATM)
- Cell Phones
- Commercial Appliance
- Computer Components
- Consumer Applications
- Containers
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, 5 mm/min) ¹¹ | 148 | MPa | ISO 527 |
| Tensile Stress (Break, 5 mm/min) ¹¹ | 147 | MPa | ISO 527 |
| Tensile Strain (Yield, 5 mm/min) ¹¹ | 3.3 | % | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 3.4 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 8700 | MPa | ISO 527 |
| Flexural Stress (Yield, at 2 mm/min) ¹¹ | 200 | MPa | ISO 178 |
| Flexural Stress (Break, 2 mm/min) ¹¹ | 198 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 7300 | MPa | ISO 178 |
Table 2 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Wear Factor Washer ¹¹ | 9 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic COF ¹¹ | 0.55 | — | ASTM D3702 Modified: Manual |
| Static COF ¹¹ | 0.5 | — | ASTM D3702 Modified: Manual |
| Density ¹¹ | 1.42 | g/cm³ | ISO 1183 |
Table 3 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.000028 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ | 0.000101 | 1/°C | ISO 11359-2 |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 197 | °C | ISO 75/Af |
Table 4 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 70 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 12 | kJ/m² | ISO 180/1A |
Table 5 of 5
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.12 - 0.2 | % |
| Melt Temperature ⁷ | 270 - 275 | °C |
| Front - Zone 3 Temperature ⁷ | 270 - 280 | °C |
| Middle - Zone 2 Temperature ⁷ | 260 - 270 | °C |
| Rear - Zone 1 Temperature ⁷ | 255 - 265 | °C |
| Mold Temperature ⁷ | 65 - 95 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |