LNP™ LUBRICOMP™ Compound DX09407H
- Chemical Family
- Polycarbonate (PC)
LNP LUBRICOMP DX09407H compound is based on High Heat Polycarbonate (PC) resin containing proprietary additive. Added features of this grade include: Wear Resistant, Healthcare.
Product families
Applications
- Medical Devices & Assemblies
- Surgical Instruments & Trays
- Healthcare Packaging
- Industrial & Transport Packaging
Product Families
- High Performance Thermoplastics
- Polycarbonates
Other characteristics
- Brand
- LNP™ LUBRICOMP™ Compound
- Polymer Name
- Polycarbonate (PC)
- Fillers Included
- Carbon Black, Glass Fiber
- Carbon Black
- Glass Fiber
- Flexural Modulus
- 2080.0 - 2080.0 MPa
- Additives Included
- Lubricant (Unspecified), Proprietary
- Lubricant (Unspecified)
- Proprietary
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Healthcare & Pharma
- Printing & Packaging
- Technology
- Plastics
- Material Features
- Electrically Conductive
- Lubricated
- Radar Absorbing
- Unreinforced
- Wear Resistant
- Plastics and Elastomers End Uses
- Medical Devices
- Medical Packaging
- Medical/Healthcare Applications
- Pharmaceutical Packaging
- Surgical Devices
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 5 mm/min) ¹¹ | 64 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 53 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 5 mm/min) ¹¹ | 6.8 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 68 | % | ASTM D638 |
| Tensile Modulus (at 5 mm/min) ¹¹ | 2230 | MPa | ASTM D638 |
| Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹ | 90 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2300 | MPa | ASTM D790 |
| Tensile Stress (Yield, 5 mm/min) ¹¹ | 64 | MPa | ISO 527 |
| Tensile Stress (Break, 5 mm/min) ¹¹ | 56 | MPa | ISO 527 |
| Tensile Strain (Yield, 5 mm/min) ¹¹ | 6.9 | % | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 111 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 2130 | MPa | ISO 527 |
Table 2 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.21 | — | ASTM D792 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.5 - 0.7 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.6 - 0.8 | % | ASTM D955 |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.21 | % | ISO 62 |
Table 3 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 139 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000074 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000077 | 1/°C | ISO 11359-2 |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 137 | °C | ISO 75/Af |
Table 4 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, at 23°C) ¹¹ | 2214 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 139 | J/m | ASTM D256 |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 191 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 11 | kJ/m² | ISO 180/1A |
Table 5 of 5
14 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 120 | °C |
| Drying Time ⁷ | 3 - 4 | Hrs |
| Drying Time (Cumulative) ⁷ | 48 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 295 - 315 | °C |
| Nozzle Temperature ⁷ | 290 - 310 | °C |
| Front - Zone 3 Temperature ⁷ | 295 - 315 | °C |
| Middle - Zone 2 Temperature ⁷ | 280 - 305 | °C |
| Rear - Zone 1 Temperature ⁷ | 270 - 295 | °C |
| Mold Temperature ⁷ | 70 - 95 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed ⁷ | 40 - 70 | rpm |