LNP™ THERMOCOMP™ AM Compound ZC004XXAR1

Name: LNP™ THERMOCOMP™ AM Compound ZC004XXAR1
Brand: LNP™ THERMOCOMP™ AM Compound

SABIC's Specialties Business LNP™ THERMOCOMP™ ZC004XXAR1 compound is based on Polyphenylene Ether / Polystyrene (PPE/PS) blend containing 20% carbon fiber for Large Format Additive Manufacturing (LFAM) applications. Added features of this grade include: Higher Stiffness vs. glass fiber, Lower Thermal Expansion, Improved Hydrolytic Stability, Higher strength to Weight Ratio, Higher Temperature Performance and improved processing vs. ABS based grades.

Product families

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Other characteristics

Brand: LNP™ THERMOCOMP™ AM Compound
Density: 1170.0 - 1170.0 kg/m³
End Uses: 3D Printing Applications, Industrial Applications, Industrial Parts
Polymer Name: PPO/PS Alloy
Processing Methods: 3D Printing, Fused Filament Fabrication, Fused Granulate Fabrication (FGF), Large Format Additive Manufacturing (LFAM)
Note: ⁿ Tensile Stiffness (K) is a structural property defined as the stress/strain in the linear region of the stress/strain curve. Value depends on the geometry/shape and boundary/surrounding conditions.
Markets: Industrial
Technology: Plastics
Fillers Included: Carbon Fiber
Material Features: Cost Effective
Dimensional Stability
Good Processability
High Hydrolytic Stability
High Stiffness
High Strength
High Strength to Weight Ratio
High Temperature Application
Country Availability: Canada
China (Mainland)
Mexico
USA
Plastics and Elastomers End Uses: 3D Printing Applications
Industrial Applications
Industrial Parts
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: 3D Printing
Fused Filament Fabrication
Fused Granulate Fabrication (FGF)
Large Format Additive Manufacturing (LFAM)

Technical data

Table 1 of 4

8 rows

Characteristic	Value	Unit	Method
Tensile Stress (at 5mm/min, XZ Orientation)	75	MPa	ASTM D638 Modified
Tensile Stress (at 5mm/min, ZX Orientation)	21	MPa	ASTM D638 Modified
Tensile Strain (at 5mm/min, XZ Orientation)	0.7	%	ASTM D638 Modified
Tensile Strain (at 5mm/min, ZX Orientation)	1	%	ASTM D638 Modified
Tensile Stiffness (at 5mm/min, XZ Orientation) ⁿ	12.2	GPa	ASTM D638 Modified
Tensile Stiffness (at 5mm/min, ZX Orientation)	2.7	GPa	ASTM D638 Modified
Flexural Stress (at 5mm/min, XZ Orientation)	36	MPa	ASTM D790 Modified
Flexural Stress (at 5mm/min, ZX Orientation)	99	MPa	ASTM D790 Modified

Table 2 of 4

1 row

Characteristic	Value	Method
Specific Gravity	1.17	ASTM D792

Table 3 of 4