NORYL™ Resin RN0206
SABIC's Specialties Business NORYL™ RN0206 resin is an non-reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This Post Consumer Recycle (PCR) based injection moldable resin containing minimum 10% PCR styrenic series resin content and is available only in black.
Product families
Applications
- Connectors
- Switches & Relays
Product Families
- Blends & Alloys
Other characteristics
- Brand
- NORYL™ Resin
- Density
- 1100.0 - 1100.0 kg/m³
- Polymer Name
- PPO/PS Alloy
- Processing Methods
- Injection Molding
- Note
ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Electrical & Electronics
- Flame Rating
- UL 94 V0
- Technology
- Plastics
- Labeling Claims
- Sustainable
- Material Features
- Amorphous
- Dimensional Stability
- High Hydrolytic Stability
- Low Moisture Absorption
- Low Shrinkage
- Low Specific Gravity
- Low Warpage
- Unreinforced
- Country Availability
- China (Mainland)
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Electrical Components
- Electrical/Electronic Applications
- Inverters
- Junction Boxes
- Micro Inverter
- Photovoltaic Device
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 73 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 14 | % | ASTM D638 |
| Flexural Stress (Yield, 2.6 mm/min, 100 mm span) ¹¹ | 100 | MPa | ASTM D790 |
| Flexural Modulus (at 2.6 mm/min, 100 mm span) ¹¹ | 2500 | MPa | ASTM D790 |
Table 2 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.1 | — | ASTM D792 |
| Melt Flow Rate (at 250°C, 10.0 kgf) ¹¹ | 5 | g/10 min | ASTM D1238 |
Table 3 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 118 | °C | ASTM D648 |
| Ball Pressure Test (approximate maximum) ¹¹ | 120 | °C | IEC 60695-10-2 |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 125 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 125 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 125 | °C | UL 746B |
Table 4 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Dielectric Strength (in air, at 3.2mm) ¹¹ | 27 | kV/mm | ASTM D149 |
| Comparative Tracking Index (UL, PLC) ¹¹ | 2 | PLC Code | UL 746A |
| Hot Wire Ignition (PLC 1) ¹¹ | min. 3 | mm | UL 746A |
Table 5 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 180 | J/m | ASTM D256 |
Table 6 of 7
14 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 105 - 110 | °C |
| Drying Time ⁷ | 3 - 4 | Hrs |
| Drying Time (Cumulative) ⁷ | 8 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 275 - 305 | °C |
| Nozzle Temperature ⁷ | 275 - 305 | °C |
| Front - Zone 3 Temperature ⁷ | 265 - 305 | °C |
| Middle - Zone 2 Temperature ⁷ | 255 - 300 | °C |
| Rear - Zone 1 Temperature ⁷ | 245 - 295 | °C |
| Mold Temperature ⁷ | 70 - 100 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed ⁷ | 20 - 100 | rpm |
Table 7 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94V-0 Flame Class Rating) ᵖ | min. 0.75 | mm | UL 94 |