NORYL™ Resin N802
SABIC's Specialties Business NORYL N802 resin is a non-reinforced blend of polyphenylene ether (PPE) + polystyrene (PS). This injection moldable grade contains non-brominated, non-chlorinated flame retardant and carries a UL94 flame rating of V2 at 0.8mm. NORYL N802 resin exhibits high flow, good dimensional stability, and low specific gravity. It is an excellent candidate for a variety of printer applications. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Electronics
- Displays
- Connectors
- Switches & Relays
Product Families
- Blends & Alloys
Other characteristics
- Brand
- NORYL™ Resin
- Density
- 1080.0 - 1080.0 kg/m³
- Polymer Name
- PPO/PS Alloy
- Flexural Modulus
- 2150.0 - 2150.0 MPa
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Consumer Goods
- Electrical & Electronics
- Flame Rating
- UL 94 V2
- Technology
- Plastics
- Labeling Claims
- Bromine-free
- Chlorine-free
- No Added PFAS
- Additives Included
- Flame Retardant
- Heat Stabilizer
- Mold Release Agent
- Material Features
- Amorphous
- Dimensional Stability
- Flame Retardant
- Good Mold Release
- Heat Stabilized
- High Flow
- High Flowability
- High Hydrolytic Stability
- Country Availability
- Canada
- Mexico
- USA
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Cell Phones
- Computer Components
- Connectors
- Displays
- Electrical Components
- Electrical/Electronic Applications
- Printer
- Tablets
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield) ¹¹ | 35 | MPa | SABIC - Japan Method |
| Tensile Strain (Break) ¹¹ | 50 | % | SABIC - Japan Method |
| Flexural Stress ¹¹ | 53 | MPa | ASTM D790 |
| Flexural Modulus ¹¹ | 2150 | MPa | ASTM D790 |
Table 2 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.08 | — | ASTM D792 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.07 | % | ASTM D570 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.5 - 0.7 | % | SABIC method |
| Melt Flow Rate (at 260°C, 2.16 kgf) ¹¹ | 21 | g/10 min | ASTM D1238 |
Table 3 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 80 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -30°C to 30°C) ¹¹ | 0.00007 | 1/°C | TMA |
Table 4 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 78 | J/m | ASTM D256 |
Table 5 of 6
13 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 - 85 | °C |
| Drying Time ⁷ | 2 - 4 | Hrs |
| Drying Time (Cumulative) ⁷ | 8 | Hrs |
| Melt Temperature ⁷ | 230 | °C |
| Nozzle Temperature ⁷ | 190 - 230 | °C |
| Front - Zone 3 Temperature ⁷ | 190 - 230 | °C |
| Middle - Zone 2 Temperature ⁷ | 190 - 230 | °C |
| Rear - Zone 1 Temperature ⁷ | 175 - 225 | °C |
| Mold Temperature ⁷ | 40 - 65 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed ⁷ | 20 - 100 | rpm |
| Shot to Cylinder Size ⁷ | 30 - 70 | % |
Table 6 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94V-2 Flame Class Rating) ʳ | min. 0.8 | mm | UL 94 |