LNP™ THERMOTUF™ Compound OF008I
- Chemical Family
- Polyphenylene Sulfide (PPS)
SABIC's Specialties Business LNP THERMOTUF OF008I compound is based on linear Polyphenylene Sulfide (PPS) resin containing 40% glass fiber. Added features of this grade include: Impact Modified. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Lawn & Garden
- Consumer Goods — Sports & Recreation
- Artificial Turf
- Consumer Electronics
- Displays
- Non-Food Consumer Packaging
- Applicators & Accessories
- Connectors
- Switches & Relays
Product Families
- High Performance Thermoplastics
Other characteristics
- Brand
- LNP™ THERMOTUF™ Compound
- Polymer Name
- Polyphenylene Sulfide (PPS)
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 11000.0 - 11000.0 MPa
- Additives Included
- Impact Modifier
- Processing Methods
- Injection Molding
- Note
ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Flame Rating
- UL 94 V0
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- High Impact Resistance
- High Modulus
- High Stiffness
- Impact Modified
- No Added PFAS
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Building Materials
- Cell Phones
- Commercial Appliance
- Computer Components
- Consumer Applications
- Containers
- Displays
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break, 5 mm/min) ¹¹ | 129 | MPa | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 1.8 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 11800 | MPa | ISO 527 |
| Flexural Stress (Break, 2 mm/min) ¹¹ | 193 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 11000 | MPa | ISO 178 |
Table 2 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.56 | g/cm³ | ISO 1183 |
Table 3 of 6
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.000013 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ | 0.000054 | 1/°C | ISO 11359-2 |
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 275 | °C | ISO 75/Bf |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 235 | °C | ISO 75/Af |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 130 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 130 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 130 | °C | UL 746B |
Table 4 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 50 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 15 | kJ/m² | ISO 180/1A |
Table 5 of 6
8 rows| Characteristic | Value | Unit |
|---|---|---|
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Drying Temperature ⁷ | 120 - 150 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Front - Zone 3 Temperature ⁷ | 330 - 345 | °C |
| Middle - Zone 2 Temperature ⁷ | 320 - 330 | °C |
| Mold Temperature ⁷ | 140 - 165 | °C |
| Rear - Zone 1 Temperature ⁷ | 305 - 315 | °C |
| Screw Speed ⁷ | 30 - 60 | rpm |
Table 6 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94V-0 Flame Class Rating) ᵖ | min. 1.5 | mm | UL 94 |