LNP™ THERMOTUF™ Compound OF008EI

Chemical Family: Polyphenylene Sulfide (PPS)

SABIC's Specialties Business LNP THERMOTUF OF008EI compound is based on linear Polyphenylene Sulfide (PPS) resin containing 40% glass fiber. Added features of this grade include: Impact Modified and Easy Molding. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.

Product families

Applications

Consumer Goods — Appliances & Electronics
Consumer Goods — Lawn & Garden
Consumer Goods — Sports & Recreation

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Consumer Electronics
Displays

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors
Switches & Relays

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics

Other characteristics

Brand: LNP™ THERMOTUF™ Compound
Polymer Name: Polyphenylene Sulfide (PPS)
Fillers Included: Glass Fiber
Flexural Modulus: 11000.0 - 11000.0 MPa
Additives Included: Impact Modifier
Processing Methods: Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Markets: Building & Construction
Consumer Goods
Electrical & Electronics
Personal Care
Printing & Packaging
Technology: Plastics
Labeling Claims: No Added PFAS
Material Features: Easy To Mold
Good Moldability
Good Processability
High Impact Resistance
High Modulus
High Stiffness
Impact Modified
No Added PFAS
Country Availability: Canada
China (Mainland)
Mexico
USA
Plastics and Elastomers End Uses: Appliances
Building Materials
Cell Phones
Commercial Appliance
Computer Components
Consumer Applications
Containers
Displays
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 5

5 rows

Characteristic	Value	Unit	Method
Tensile Stress (Break, 5 mm/min) ¹¹	145	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	1.8	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	12500	MPa	ISO 527
Flexural Stress (Yield, at 2 mm/min) ¹¹	210	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	11000	MPa	ISO 178

Table 2 of 5

2 rows

Characteristic	Value	Unit	Method
Mold Shrinkage (flow) ᵍ ¹¹	0.15	%	SABIC method
Density ¹¹	1.6	g/cm³	ISO 1183

Table 3 of 5

3 rows

Characteristic	Value	Unit	Method
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹	0.000015	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹	0.000047	1/°C	ISO 11359-2
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	263	°C	ISO 75/Af

Table 4 of 5