LNP™ THERMOTUF™ Compound PF003IU
- Chemical Family
- Polyamides
SABIC's Specialties Business LNP™ THERMOTUF™ PF003IU compound is based on Nylon 6 resin containing 15% glass fiber. Added features of this grade include: Impact Modified and UV Stabilized.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Lawn & Garden
- Consumer Goods — Sports & Recreation
- Interior
- Artificial Turf
- Consumer Electronics
- Displays
- Non-Food Consumer Packaging
- Applicators & Accessories
- Connectors
- Housings & Enclosures
- Switches & Relays
Product Families
- Polyamides
Other characteristics
- Brand
- LNP™ THERMOTUF™ Compound
- Polymer Name
- Polyamide 6 (PA 6)
- Fillers Included
- Glass Fiber
- Additives Included
Heat Stabilizer, Impact Modifier, Mold Release Agent, UV Stabilizer; Heat Stabilizer; Impact Modifier; Mold Release Agent; UV Stabilizer
- Processing Methods
- Injection Molding
- Note
⁷ Параметры литья под давлением указаны только в качестве общих рекомендаций. Они могут не применяться или требовать корректировки в конкретных ситуациях, таких как малые объемы впрыска, литье крупногабаритных деталей, литье тонкостенных деталей и газовое литье.. ¹¹ Информация, указанная в технических паспортах, должна использоваться только в качестве ориентировочной для целей выбора материала и не должна использоваться в качестве спецификации или для проектирования деталей или пресс-форм.
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Technology
- Plastics
- Material Features
- Good Mold Release
- Good UV Stability
- Good Weather Stability
- Heat Stabilized
- High Impact Resistance
- High Modulus
- Impact Modified
- UV Resistant
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Interior Parts
- Building Materials
- Cell Phones
- Computer Components
- Consumer Applications
- Containers
- Displays
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 4
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 4100 | MPa | ASTM D790 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 145 | MPa | ASTM D790 |
| Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 103 | MPa | ASTM D638 |
Table 2 of 4
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 197 | °C | ASTM D648 |
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 215 | °C | ASTM D648 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 201 | °C | ASTM D1525 |
Table 3 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 65 | J/m | ASTM D256 |
| Izod Impact (Unnotched, at 23°C) ¹¹ | 610 | J/m | ASTM D4812 |
Table 4 of 4
11 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 100 - 110 | °C |
| Drying Time ⁷ | 3 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 250 - 265 | °C |
| Nozzle Temperature ⁷ | 245 - 260 | °C |
| Front - Zone 3 Temperature ⁷ | 250 - 265 | °C |
| Middle - Zone 2 Temperature ⁷ | 245 - 260 | °C |
| Rear - Zone 1 Temperature ⁷ | 240 - 255 | °C |
| Mold Temperature ⁷ | 65 - 90 | °C |
| Screw Speed ⁷ | 50 - 80 | rpm |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |