NORYL PPX™ Resin PPX630F
SABIC's Specialties Business NORYL PPX630F resin is a 30% glass fiber reinforced alloy of polyphenylene ether (PPE) + polypropylene (PP). This injection moldable grade is NSF 61 certified and exhibits high elongation and stiffness along with temperature performance, impact resistance, hydrolytic and dimensional stability. NORYL PPX630F resin is an excellent candidate for copper and brass replacement in water management applications such as boiler manifolds, condensers, and hydro blocks. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Pipes & Plumbing
- Water Treatment
Product Families
- Blends & Alloys
Other characteristics
- Brand
- NORYL PPX™ Resin
- Density
- 1190.0 - 1190.0 kg/m³
- Polymer Name
- PPE/PP Alloy
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- Markets
- Building & Construction
- Industrial
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Labeling Claims
- Food Contact Acceptable
- No Added PFAS
- Fillers Included
- Glass Fiber
- Additives Included
- Heat Stabilizer
- Impact Modifier
- Material Features
- Chemical Resistant
- Dimensional Stability
- Food Contact Acceptable
- Heat Stabilized
- High Hydrolytic Stability
- High Impact Resistance
- High Stiffness
- High Strength
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Certifications and Compliance
- NSF Standard 61 for Drinking Water
- UL 94
- Plastics and Elastomers End Uses
- Faucet System Components
- Filters
- Fittings
- Gears
- Potable Water Applications
- Pump Parts
- Water Management
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 5 mm/min) ¹¹ | 79 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 79 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 7.7 | % | ASTM D638 |
| Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹ | 129 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 5550 | MPa | ASTM D790 |
Table 2 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.19 | — | ASTM D792 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.2 - 0.23 | % | SABIC method |
| Mold Shrinkage (xflow, 3.2 mm) ᵍ ¹¹ | 0.25 - 0.76 | % | SABIC method |
| Melt Flow Rate (at 260°C, 5.0 kgf) ¹¹ | 2.6 | g/10 min | ASTM D1238 |
Table 3 of 6
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat Softening Temperature (Rate B/50) ¹¹ | 162 | °C | ASTM D1525 |
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 155 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 133 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.0000144 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.0000774 | 1/°C | ASTM E831 |
Table 4 of 6
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, at 23°C) ¹¹ | 827 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 165 | J/m | ASTM D256 |
| Izod Impact (Notched, at -30°C) ¹¹ | 101 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 19 | J | ASTM D3763 |
| Instrumented Dart Impact Total Energy (at -30°C) ¹¹ | 20 | J | ASTM D3763 |
Table 5 of 6
14 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 65 - 75 | °C |
| Drying Time ⁷ | 2 - 4 | Hrs |
| Drying Time (Cumulative) ⁷ | 8 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 260 - 300 | °C |
| Nozzle Temperature ⁷ | 260 - 300 | °C |
| Front - Zone 3 Temperature ⁷ | 255 - 295 | °C |
| Middle - Zone 2 Temperature ⁷ | 250 - 290 | °C |
| Rear - Zone 1 Temperature ⁷ | 245 - 290 | °C |
| Mold Temperature ⁷ | 40 - 65 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed ⁷ | 20 - 100 | rpm |
Table 6 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94HB Flame Class Rating) ᵖ | min. 1.5 | mm | UL 94 |