LNP™ COLORCOMP™ Compound AX98567H
- Chemical Family
- Acrylonitrile Butadiene Styrene (ABS)Styrenics
SABIC's Specialties Business LNP COLORCOMP AX98567H compound is based on Acrylonitrile Butadiene Styrene (ABS) resin. Added features of this grade include: Healthcare. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Medical Devices & Assemblies
- Surgical Instruments & Trays
- Healthcare Packaging
- Industrial & Transport Packaging
Product Families
- Styrenics
Other characteristics
- Brand
- LNP™ COLORCOMP™ Compound
- Polymer Name
- Acrylonitrile Butadiene Styrene (ABS)
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Color
- Custom
- Markets
- Healthcare & Pharma
- Printing & Packaging
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Excellent Aesthetics
- Good Aesthetics
- Good Surface Appearance
- High Durability
- No Added PFAS
- Unreinforced
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Medical Devices
- Medical Packaging
- Medical/Healthcare Applications
- Pharmaceutical Packaging
- Surgical Devices
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, 5 mm/min) ¹¹ | 52 | MPa | ISO 527 |
| Tensile Strain (Yield, 5 mm/min) ¹¹ | 2 | % | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 15 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 2500 | MPa | ISO 527 |
| Flexural Stress ¹¹ | 75 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 2600 | MPa | ISO 178 |
Table 2 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.06 | — | ASTM D792 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.4 - 0.6 | % | ISO 294 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.4 - 0.6 | % | ISO 294 |
| Melt Volume Rate (at 220°C, 10.0 kg) ¹¹ | 16 | cm³/10 min | ISO 1133 |
| Melt Volume Rate (at 230°C, 10.0 kg) ¹¹ | 27 | cm³/10 min | ISO 1133 |
Table 3 of 7
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.00008 | 1/°C | ISO 11359-2 |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 80 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 80 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 80 | °C | UL 746B |
Table 4 of 7
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volume Resistivity ¹¹ | 1.00E+16 | Ω.cm | IEC 60093 |
| Surface Resistivity (ROA) ¹¹ | 1.00E+16 | Ω | IEC 60093 |
| Hot Wire Ignition (PLC 4) ¹¹ | min. 1.5 | mm | UL 746A |
| High Ampere Arc Ignition (PLC 0) ¹¹ | min. 1.5 | mm | UL 746A |
| High Voltage Arc Track Rate (PLC) ¹¹ | 1 | PLC Code | UL 746A |
| Arc Resistance (Tungsten, PLC) ¹¹ | 6 | PLC Code | ASTM D495 |
Table 5 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Charpy Impact (Unnotched, at -30°C) ¹¹ | 70 | kJ/m² | ISO 179/2C |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 12 | kJ/m² | ISO 180/1A |
| Charpy Impact (Notched, at 23°C) ¹¹ | 11 | kJ/m² | ISO 179/2C |
Table 6 of 7
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.05 - 0.1 | % |
| Melt Temperature ⁷ | 260 | °C |
| Front - Zone 3 Temperature ⁷ | 265 - 275 | °C |
| Middle - Zone 2 Temperature ⁷ | 230 - 245 | °C |
| Rear - Zone 1 Temperature ⁷ | 205 - 215 | °C |
| Mold Temperature ⁷ | 70 - 80 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |
Table 7 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94HB Flame Class Rating) ᵖ | min. 1.5 | mm | UL 94 |