LNP™ COLORCOMP™ Compound W1000EXP
- Chemical Family
- Polyesters
SABIC's Specialties Business LNP COLORCOMP W1000EXP compound is based on unfilled Polybutylene Terephthalate (PBT) resin. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Housewares
- Consumer Goods — Sports & Recreation
- Interior
- Consumer Electronics
- Displays
- Non-Food Consumer Packaging
- Applicators & Accessories
Product Families
- Polyesters & Copolyesters
Other characteristics
- Brand
- LNP™ COLORCOMP™ Compound
- Polymer Name
- Polybutylene Terephthalate (PBT)
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Color
- Custom
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Excellent Aesthetics
- Good Aesthetics
- Good Surface Appearance
- No Added PFAS
- Unreinforced
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Automotive Applications
- Automotive Interior Parts
- Cell Phones
- Commercial Appliance
- Computer Components
- Consumer Applications
- Containers
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 51 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 51 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 200 | % | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 82 | MPa | ASTM D790 |
| Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹ | 82 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2340 | MPa | ASTM D790 |
| Hardness (Rockwell R) ¹¹ | 117 | — | ASTM D785 |
Table 2 of 7
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.31 | — | ASTM D792 |
| Specific Volume ¹¹ | 0.76 | cm³/g | ASTM D792 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.08 | % | ASTM D570 |
| Mold Shrinkage (flow, 0.75-2.3 mm) ᵍ ¹¹ | 0.9 - 1.6 | % | SABIC method |
| Mold Shrinkage (flow, 2.3-4.6 mm) ᵍ ¹¹ | 1.5 - 2.3 | % | SABIC method |
| Mold Shrinkage (xflow, 0.75-2.3 mm) ᵍ ¹¹ | 1 - 1.7 | % | SABIC method |
| Mold Shrinkage (xflow, 2.3-4.6 mm) ᵍ ¹¹ | 1.6 - 2.4 | % | SABIC method |
| Melt Viscosity ¹¹ | 6.00E+02 | Pa-s | SABIC method |
Table 3 of 7
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 0.45 MPa, 6.4 mm, Unannealed) ¹¹ | 154 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 54 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000081 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at 60°C to 138°C, flow) ¹¹ | 0.000139 | 1/°C | ASTM E831 |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 120 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 120 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 140 | °C | UL 746B |
Table 4 of 7
16 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volume Resistivity ¹¹ | min. 4.E+16 | Ω.cm | ASTM D257 |
| Dielectric Strength (in air, at 1.6mm) ¹¹ | 23.2 | kV/mm | ASTM D149 |
| Dielectric Strength (in air, at 3.2mm) ¹¹ | 15.7 | kV/mm | ASTM D149 |
| Dielectric Strength (in oil, at 1.6mm) ¹¹ | 23.2 | kV/mm | ASTM D149 |
| Dielectric Strength (in oil, at 3.2mm) ¹¹ | 15.7 | kV/mm | ASTM D149 |
| Relative Permittivity (100 Hz) ¹¹ | 3.3 | — | ASTM D150 |
| Relative Permittivity (1 MHz) ¹¹ | 3.1 | — | ASTM D150 |
| Dissipation Factor (at 100 Hz) ¹¹ | 0.002 | — | ASTM D150 |
| Dissipation Factor (at at 1 MHz) ¹¹ | 0.02 | — | ASTM D150 |
| Comparative Tracking Index (UL, PLC) ¹¹ | 0 | PLC Code | UL 746A |
| Hot Wire Ignition (PLC 2) ¹¹ | min. 6 | mm | UL 746A |
| Hot Wire Ignition (PLC 3) ¹¹ | min. 3 | mm | UL 746A |
Table 5 of 7
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, at 23°C) ¹¹ | 1602 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 53 | J/m | ASTM D256 |
| Color (at 23°C) ¹¹ | 40 | J | ASTM D3029 |
| Modified Gardner (at 23°C) ¹¹ | 40 | J | ASTM D3029 |
Table 6 of 7
14 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 120 | °C |
| Drying Time ⁷ | 3 - 4 | Hrs |
| Drying Time (Cumulative) ⁷ | 12 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 245 - 260 | °C |
| Nozzle Temperature ⁷ | 240 - 255 | °C |
| Front - Zone 3 Temperature ⁷ | 245 - 260 | °C |
| Middle - Zone 2 Temperature ⁷ | 240 - 255 | °C |
| Rear - Zone 1 Temperature ⁷ | 230 - 250 | °C |
| Mold Temperature ⁷ | 50 - 75 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed ⁷ | 50 - 100 | rpm |
Table 7 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94HB Flame Class Rating) ᵖ | min. 1.5 | mm | UL 94 |
| UL Recognized (94HB Flame Class Rating) ᵖ | min. 0.84 | mm | UL 94 |