LNP™ COLORCOMP™ Compound D1000EXJ
- Chemical Family
- Polycarbonate (PC)
SABIC's Specialties Business LNP COLORCOMP D1000EXJ compound is based on unfilled Polycarbonate (PC) resin. Added features of this grade include: Healthcare, Low Extractable, Food Contact Compliant and UL rated HB.
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics
Building & Construction — Building Materials
- Pipes & Plumbing
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
Healthcare & Pharma — Medical
- Dental
- Medical Devices & Assemblies
- Surgical Instruments & Trays
Printing & Packaging — Packaging
- Food & Beverage Packaging
- Healthcare Packaging
- Industrial & Transport Packaging
- Non-Food Consumer Packaging
Product Families
Plastics — Engineering & Specialty Polymers
- High Performance Thermoplastics
- Polycarbonates
Other characteristics
- Brand
- LNP™ COLORCOMP™ Compound
- Polymer Name
- Polycarbonate (PC)
- Flexural Modulus
- 2250.0 - 2250.0 MPa
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Color
- Custom
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Healthcare & Pharma
- Printing & Packaging
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Labeling Claims
- Food Contact Acceptable
- Material Features
- Excellent Aesthetics
- Food Contact Acceptable
- Good Aesthetics
- Good Surface Appearance
- Heat Stabilized
- High Durability
- Low Extractables
- Low Leachable
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Building Materials
- Consumer Applications
- Dental Applications
- Food Packaging
- Home Appliances
- Hoses
- Medical Devices
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 8
16 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 62 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 68 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ | 7 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 130 | % | ASTM D638 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 2300 | MPa | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 96 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2340 | MPa | ASTM D790 |
| Hardness (Rockwell M) ¹¹ | 70 | — | ASTM D785 |
| Hardness (Rockwell R) ¹¹ | 118 | — | ASTM D785 |
| Tensile Stress (Yield, 50 mm/min) ¹¹ | 61 | MPa | ISO 527 |
| Tensile Stress (Break, 50 mm/min) ¹¹ | 73 | MPa | ISO 527 |
| Tensile Strain (Yield, 50 mm/min) ¹¹ | 6 | % | ISO 527 |
Table 2 of 8
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.2 | — | ASTM D792 |
| Density ¹¹ | 1.19 | g/cm³ | ISO 1183 |
| Density ¹¹ | 1.19 | g/cm³ | ASTM D792 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.15 | % | ASTM D570 |
| Water Absorption (at 23°C, saturated) ¹¹ | 0.26 | % | ISO 62-1 |
| Water Absorption (at 23°C, saturated) ¹¹ | 0.35 | % | ASTM D570 |
| Water Absorption (Equilibrium, at 100°C) ¹¹ | 0.58 | % | ASTM D570 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.5 - 0.7 | % | SABIC method |
| Melt Flow Rate (at 300°C, 1.2 kgf) ¹¹ | 10.5 | g/10 min | ASTM D1238 |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.1 | % | ISO 62 |
| Melt Volume Rate (at 300°C, 1.2 kg) ¹¹ | 10 | cm³/10 min | ISO 1133 |
Table 3 of 8
18 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat Softening Temperature (Rate B/50) ¹¹ | 143 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 154 | °C | ASTM D1525 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 126 | °C | ASTM D648 |
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 137 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000078 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000078 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000076 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000076 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -40°C to 95°C, flow) ¹¹ | 0.000068 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 95°C, xflow) ¹¹ | 0.000068 | 1/°C | ASTM E831 |
| Specific Heat ¹¹ | 1.25 | J/g-°C | ASTM C351 |
| Thermal Conductivity ¹¹ | 0.19 | W/m-°C | ASTM C177 |
Table 4 of 8
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volume Resistivity ¹¹ | min. 1.E+17 | Ω.cm | ASTM D257 |
| Dielectric Strength (in air, at 3.2mm) ¹¹ | 14.9 | kV/mm | ASTM D149 |
| Relative Permittivity (50/60 Hz) ¹¹ | 3.17 | — | ASTM D150 |
| Relative Permittivity (1 MHz) ¹¹ | 2.96 | — | ASTM D150 |
| Dissipation Factor (at 50/60 Hz) ¹¹ | 0.0009 | — | ASTM D150 |
| Dissipation Factor (at at 1 MHz) ¹¹ | 0.01 | — | ASTM D150 |
| Comparative Tracking Index (UL, PLC) ¹¹ | 2 | PLC Code | UL 746A |
| Hot Wire Ignition (PLC 2) ¹¹ | min. 1.5 | mm | UL 746A |
| Hot Wire Ignition (PLC 3) ¹¹ | min. 1.1 | mm | UL 746A |
| High Ampere Arc Ignition (PLC 1) ¹¹ | min. 1.5 | mm | UL 746A |
| High Ampere Arc Ignition (PLC 2) ¹¹ | min. 1.1 | mm | UL 746A |
| High Voltage Arc Track Rate (PLC) ¹¹ | 2 | PLC Code | UL 746A |
Table 5 of 8
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Light Transmission (at 2.54 mm) ¹¹ | 88 | % | ASTM D1003 |
| Haze (at 2.54 mm) ¹¹ | 1 | % | ASTM D1003 |
| Refractive Index ¹¹ | 1.586 | — | ASTM D542 |
Table 6 of 8
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, at 23°C) ¹¹ | 3204 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 801 | J/m | ASTM D256 |
| Izod Impact (Notched, at -30°C) ¹¹ | 220 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 88 | J | ASTM D3763 |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 71 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at -30°C) ¹¹ | 10 | kJ/m² | ISO 180/1A |
| Charpy Impact (at 23°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹ | 82 | kJ/m² | ISO 179/1eU |
Table 7 of 8
14 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 120 | °C |
| Drying Time ⁷ | 3 - 4 | Hrs |
| Drying Time (Cumulative) ⁷ | 48 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 295 - 315 | °C |
| Nozzle Temperature ⁷ | 290 - 310 | °C |
| Front - Zone 3 Temperature ⁷ | 295 - 315 | °C |
| Middle - Zone 2 Temperature ⁷ | 280 - 305 | °C |
| Rear - Zone 1 Temperature ⁷ | 270 - 295 | °C |
| Mold Temperature ⁷ | 70 - 95 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed ⁷ | 40 - 70 | rpm |
Table 8 of 8
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94HB Flame Class Rating) ᵖ | min. 0.7 | mm | UL 94 |
| Oxygen Index (LOI) ᵖ | 25 | % | ASTM D2863 |