LNP™ THERMOCOMP™ AM Compound DC004XXA11

Chemical Family: Polycarbonate (PC)

SABIC's Specialties Business LNP™ THERMOCOMP™ AM DC004XXA11is a compound based on High Heat PC copolymer resin containing 20% carbon fiber for Large Format Additive manufacturing (LFAM) applications, including mid-temperature autoclaving tooling. This compound can offer higher temperature performance than standard PC and avoid some of the processing challenges associated with high temperature materials.

Product families

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Other characteristics

Brand: LNP™ THERMOCOMP™ AM Compound
Density: 1290.0 - 1290.0 kg/m³
Polymer Name: Polycarbonate (PC)
Fillers Included: Carbon Fiber
Processing Methods: 3D Printing, Fused Filament Fabrication, Fused Granulate Fabrication (FGF), Large Format Additive Manufacturing (LFAM)
Note: ⁿ Tensile Stiffness (K) is a structural property defined as the stress/strain in the linear region of the stress/strain curve. Value depends on the geometry/shape and boundary/surrounding conditions.
Markets: Industrial
Technology: Plastics
Material Features: Cost Effective
Heat Resistance
High Ductility
High Temperature Strength
Low Warpage
Very Good Heat Resistance
Country Availability: Canada
China (Mainland)
Mexico
USA
Plastics and Elastomers End Uses: 3D Printing Applications
Automotive Body Panel
Industrial Applications
Industrial Parts
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: 3D Printing
Fused Filament Fabrication
Fused Granulate Fabrication (FGF)
Large Format Additive Manufacturing (LFAM)

Technical data

Table 1 of 4

8 rows

Characteristic	Value	Unit	Method
Tensile Stress (at 5mm/min, XZ Orientation)	86	MPa	ASTM D638 Modified
Tensile Stress (at 5mm/min, ZX Orientation)	19	MPa	ASTM D638 Modified
Tensile Strain (at 5mm/min, XZ Orientation)	1.2	%	ASTM D638 Modified
Tensile Strain (at 5mm/min, ZX Orientation)	1.2	%	ASTM D638 Modified
Tensile Stiffness (at 5mm/min, XZ Orientation) ⁿ	8.5	GPa	ASTM D638 Modified
Tensile Stiffness (at 5mm/min, ZX Orientation)	1.8	GPa	ASTM D638 Modified
Flexural Stress (at 5mm/min, XZ Orientation)	28	MPa	ASTM D790 Modified
Flexural Stress (at 5mm/min, ZX Orientation)	109	MPa	ASTM D790 Modified

Table 2 of 4

1 row

Characteristic	Value	Method
Specific Gravity	1.29	ASTM D792

Table 3 of 4