LNP™ ELCRES™ FXP1430
SABIC's Specialties Business ELCRES FXP1430 is PC-siloxane copolymer in special "Luster Plus" pearlescent appearance, which is part of the VisualFx family. This product features vivid and resplendent look with improved ductility and medium flow. UV stabilized. Color package may affect performance. Applications include housing of consumer electronics, cosmetic packaging, automotive interior decoration, etc.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Housewares
- Consumer Goods — Sports & Recreation
- Interior
- Automotive Electronics
- Consumer Electronics
- Displays
- Industrial & Transport Packaging
- Non-Food Consumer Packaging
- Batteries
- Housings & Enclosures
Product Families
- High Performance Thermoplastics
- Polycarbonates
Other characteristics
- Brand
- LNP™ ELCRES
- Polymer Name
- Polycarbonate-Siloxane Copolymer
- Flexural Modulus
- 2150.0 - 2150.0 MPa
- Additives Included
- UV Stabilizer
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Color
- Custom
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Printing & Packaging
- Technology
- Plastics
- Material Features
- Excellent Aesthetics
- Good Aesthetics
- Good Bright Luster
- Good Surface Appearance
- Low Temperature Impact Resistance
- UV Stabilized
- Unreinforced
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers End Uses
- AC Charging Cabinet
- Appliances
- Automotive Applications
- Automotive Interior Parts
- Automotive Under The Hood
- Batteries
- Cell Phones
- Commercial Appliance
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
18 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 61 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 56 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ | 6.2 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 79 | % | ASTM D638 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 2150 | MPa | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 94 | MPa | ASTM D790 |
| Flexural Strength (at 1.3 mm/min, 50 mm span) ¹¹ | 94 | MPa | ASTM D790 |
| Flexural Stress (at 5% strain, 1.3 mm/min, 50 mm span) ¹¹ | 87 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2240 | MPa | ASTM D790 |
| Tensile Stress (Yield, 50 mm/min) ¹¹ | 61 | MPa | ISO 527 |
| Tensile Stress (Break, 50 mm/min) ¹¹ | 5.50E+01 | MPa | ISO 527 |
| Tensile Strain (Yield, 50 mm/min) ¹¹ | 5.3 | % | ISO 527 |
Table 2 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.185 | — | ASTM D792 |
| Melt Flow Rate (at 300°C, 1.2 kgf) ¹¹ | 12 | g/10 min | ASTM D1238 |
| Melt Volume Rate (at 300°C, 1.2 kg) ¹¹ | 11.7 | cm³/10 min | ASTM D1238 |
| Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.037 | % | ISO 62-4 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.15 | % | ISO 62-1 |
| Mold Shrinkage (flow) ᵍ ¹¹ | 0.72 | % | SABIC method |
| Mold Shrinkage (xflow) ᵍ ¹¹ | 0.75 | % | SABIC method |
Table 3 of 5
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 127 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 113 | °C | ASTM D648 |
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 129 | °C | ISO 75/Bf |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 114 | °C | ISO 75/Af |
| Vicat Softening Temperature (Rate A/50) ¹¹ | 142 | °C | ASTM D1525 |
| Vicat Softening Temperature (Rate B/120) ¹¹ | 135 | °C | ASTM D1525 |
| Vicat Softening Temperature (Rate B/120) ¹¹ | 133.5 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 133 | °C | ISO 306 |
| Coefficient of Thermal Expansion (at -40°C to 95°C, flow) ¹¹ | 0.00007 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 95°C, xflow) ¹¹ | 0.000081 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at 23°C to 80°C, flow) ¹¹ | 0.000079 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 80°C, xflow) ¹¹ | 0.000087 | 1/°C | ISO 11359-2 |
Table 4 of 5
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, at 23°C) ¹¹ | 2170 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 578 | J/m | ASTM D256 |
| Izod Impact (Notched, at 0°C) ¹¹ | 131 | J/m | ASTM D256 |
| Izod Impact (Notched, at -10°C) ¹¹ | 129 | J/m | ASTM D256 |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 181 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 14.4 | kJ/m² | ISO 180/1A |
| Charpy Impact (at 23°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹ | 131.6 | kJ/m² | ISO 179/1eU |
| Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 20.8 | kJ/m² | ISO 179/1eA |
Table 5 of 5
9 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 120 | °C |
| Drying Time ⁷ | 3 - 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 295 - 315 | °C |
| Nozzle Temperature ⁷ | 290 - 310 | °C |
| Front - Zone 3 Temperature ⁷ | 295 - 315 | °C |
| Middle - Zone 2 Temperature ⁷ | 280 - 305 | °C |
| Rear - Zone 1 Temperature ⁷ | 260 - 280 | °C |
| Mold Temperature ⁷ | 70 - 95 | °C |