NORYL™ Resin SE1GFN3
SABIC's Specialties Business NORYL SE1GFN3 resin is a 30% glass fiber reinforced blend of polyphenylene ether (PPE) + polystyrene (PS). This injection moldable grade contains non-brominated, non-chlorinated flame retardant and carries a UL94 flame rating of V1 at 1.5mm along with UL746C Outdoor Suitability rating of F1 and RTI of 110C. NORYL SE1GFN3 exhibits high heat resistance, good dielectric strength, dimensional stability, hydrolytic stability, and very low moisture absorption. This material is an excellent candidate for a variety of applications such as solar frames, unattended power supply (UPS) inverter/charger, indoor and outdoor electrical enclosures / housings / connectors, and wall plates / sockets / switches. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Electrical & Electronic Systems
- Automotive Electronics
- Consumer Electronics
- Displays
- Batteries
- Connectors
- Switches & Relays
- Terminal Blocks Plugs & Sockets
- Renewable Energy
Product Families
- Blends & Alloys
Other characteristics
- Brand
- NORYL™ Resin
- Density
- 1310.0 - 1310.0 kg/m³
- Polymer Name
- PPO/PS Alloy
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Industrial
- Flame Rating
- UL 94 5VA
- UL 94 V0
- UL 94 V1
- Technology
- Plastics
- Labeling Claims
- Bromine-free
- Chlorine-free
- No Added PFAS
- Fillers Included
- Glass Fiber
- Additives Included
- Flame Retardant
- Material Features
- Amorphous
- Dimensional Stability
- Flame Retardant
- Good Stiffness
- High Hydrolytic Stability
- Low Moisture Absorption
- Low Shrinkage
- Low Specific Gravity
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- AC Charging Cabinet
- Automotive Under The Hood
- Batteries
- Cell Phones
- Computer Components
- Connectors
- Displays
- Electric Vehicles
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Taber Abrasion (CS-17, 1 kg) ¹¹ | 55 | mg/1000cy | SABIC method |
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 120 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 5 | % | ASTM D638 |
| Tensile Stress (Break, 5 mm/min) ¹¹ | 105 | MPa | ISO 527 |
| Flexural Stress (Yield, 2.6 mm/min, 100 mm span) ¹¹ | 172 | MPa | ASTM D790 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 2 | % | ISO 527 |
| Flexural Modulus (at 2.6 mm/min, 100 mm span) ¹¹ | 7790 | MPa | ASTM D790 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 8000 | MPa | ISO 527 |
| Flexural Stress (Break, 2 mm/min) ¹¹ | 130 | MPa | ISO 178 |
| Hardness (Rockwell L) ¹¹ | 108 | — | ASTM D785 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 6000 | MPa | ISO 178 |
| Ball Indentation Hardness (H358/30) ¹¹ | 130 | MPa | ISO 2039-1 |
Table 2 of 7
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.31 | — | ASTM D792 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.06 | % | ASTM D570 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.1 - 0.4 | % | SABIC method |
| Mold Shrinkage (on Tensile Bar, flow) ᵍ ¹¹ | 0.1 - 0.3 | % | SABIC method |
| Density ¹¹ | 1.29 | g/cm³ | ISO 1183 |
| Water Absorption (at 23°C, saturated) ¹¹ | 0.23 | % | ISO 62-1 |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.07 | % | ISO 62 |
| Melt Volume Rate (at 280°C, 10.0 kg) ¹¹ | 9 | cm³/10 min | ISO 1133 |
Table 3 of 7
20 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 0.45 MPa, 6.4 mm, Unannealed) ¹¹ | 140 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 135 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 95°C, flow) ¹¹ | 0.0000252 | 1/°C | ASTM E831 |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 110 | °C | UL 746B |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000037 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000037 | 1/°C | ISO 11359-2 |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 105 | °C | UL 746B |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000055 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000055 | 1/°C | ISO 11359-2 |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 110 | °C | UL 746B |
| Thermal Conductivity ¹¹ | 0.28 | W/m-°C | ISO 8302 |
| Coefficient of Thermal Expansion (at 23°C to 80°C, flow) ¹¹ | 0.00003 | 1/°C | ISO 11359-2 |
Table 4 of 7
22 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Dielectric Strength (in oil, at 3.2mm) ¹¹ | 16 | kV/mm | IEC 60243-1 |
| Dielectric Strength (in oil, at 3.2mm) ¹¹ | 20.8 | kV/mm | ASTM D149 |
| Relative Permittivity (50/60 Hz) ¹¹ | 3.15 | — | ASTM D150 |
| Relative Permittivity (50/60 Hz) ¹¹ | 3.1 | — | IEC 60250 |
| Dissipation Factor (at 50/60 Hz) ¹¹ | 0.002 | — | ASTM D150 |
| Dissipation Factor (at 50/60 Hz) ¹¹ | 0.008 | — | IEC 60250 |
| High Voltage Arc Track Rate (PLC) ¹¹ | 4 | PLC Code | UL 746A |
| Comparative Tracking Index (UL, PLC) ¹¹ | 3 | PLC Code | UL 746A |
| High Ampere Arc Ignition (PLC 2) ¹¹ | min. 1.5 | mm | UL 746A |
| High Ampere Arc Ignition (PLC 2) ¹¹ | min. 1.47 | mm | UL 746A |
| Hot Wire Ignition (PLC 0) ¹¹ | min. 1.5 | mm | UL 746A |
| Hot Wire Ignition (PLC 0) ¹¹ | min. 1.47 | mm | UL 746A |
Table 5 of 7
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 117 | J/m | ASTM D256 |
| Izod Impact (Notched, at -40°C) ¹¹ | 96 | J/m | ASTM D256 |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 25 | kJ/m² | ISO 180/1U |
| Izod Impact (Unnotched, 80*10*4, at -30°C) ¹¹ | 25 | kJ/m² | ISO 180/1U |
| Charpy Impact (at 23°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹ | 30 | kJ/m² | ISO 179/1eU |
| Charpy Impact (at -30°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹ | 30 | kJ/m² | ISO 179/1eU |
Table 6 of 7
21 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 110 - 120 | °C |
| Drying Time ⁷ | 3 - 4 | Hrs |
| Drying Time ⁷ | 2 - 3 | Hrs |
| Drying Time (Cumulative) ⁷ | 8 | Hrs |
| Melt Temperature ⁷ | 300 - 320 | °C |
| Melt Temperature ⁷ | 300 - 325 | °C |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Nozzle Temperature ⁷ | 280 - 300 | °C |
| Nozzle Temperature ⁷ | 300 - 325 | °C |
| Front - Zone 3 Temperature ⁷ | 290 - 325 | °C |
| Front - Zone 3 Temperature ⁷ | 300 - 320 | °C |
| Middle - Zone 2 Temperature ⁷ | 280 - 300 | °C |
Table 7 of 7
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94V-0 Flame Class Rating) ʳ | min. 6 | mm | UL 94 |
| UL Recognized (94V-0 Flame Class Rating) ʳ | min. 6.1 | mm | UL 94 |
| UL Recognized (94V-1 Flame Class Rating) ʳ | min. 1.5 | mm | UL 94 |
| UL Recognized (94V-1 Flame Class Rating) ʳ | min. 0.71 | mm | UL 94 |
| UL Recognized (94V-1 Flame Class Rating) ʳ | min. 1.47 | mm | UL 94 |
| Oxygen Index (LOI) ʳ | 35.5 | % | ASTM D2863 |
| Oxygen Index (LOI) ʳ | 31 | % | ISO 4589 |
| UL Recognized (94-5VA Flame Class Rating) ʳ | min. 3 | mm | UL 94 |
| Glow Wire Flammability Index (passes at 960°C) ʳ | 3.2 | mm | IEC 60695-2-12 |
| UV-light (Water exposure/immersion) ʳ | F2 | — | UL 746C |