LNP™ LUBRICOMP™ Compound EFL34HL
- Chemical Family
- Polyetherimide (PEI)Polyimides (PI)
SABIC's Specialties Business LNP LUBRICOMP EFL34HL compound is based on Polyetherimide (PEI) resin containing 20% glass fiber, 15% PTFE. Added features of this grade include: Wear Resistant, Low Extractable.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Pipes & Plumbing
- Consumer Electronics
- Medical Devices & Assemblies
- Surgical Instruments & Trays
- Food & Beverage Packaging
- Healthcare Packaging
- Industrial & Transport Packaging
- Non-Food Consumer Packaging
- Housings & Enclosures
Product Families
- High Performance Thermoplastics
Other characteristics
- Brand
- LNP™ LUBRICOMP™ Compound
- Polymer Name
- Polyether Imide (PEI)
- Fillers Included
- Glass Fiber, PTFE
- Glass Fiber
- PTFE
- Flexural Modulus
- 7510.0 - 7510.0 MPa
- Additives Included
- Lubricant (PTFE)
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Healthcare & Pharma
- Printing & Packaging
- Technology
- Plastics
- Labeling Claims
- Food Contact Acceptable
- Material Features
- Food Contact Acceptable
- Friction Resistant
- High Temperature Resistance
- Low Extractables
- Low Leachable
- Very Good Heat Resistance
- Wear Resistant
- Plastics and Elastomers End Uses
- Appliances
- Building Materials
- Consumer Applications
- Covers
- Enclosure
- Food Packaging
- Home Appliances
- Hoses
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break) ¹¹ | 113 | MPa | ISO 527 |
| Tensile Stress (Break) ¹¹ | 113 | MPa | ASTM D638 |
| Tensile Strain (Break) ¹¹ | 2.2 | % | ASTM D638 |
| Tensile Strain (Break) ¹¹ | 2.2 | % | ISO 527 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 7580 | MPa | ASTM D638 |
| Flexural Stress ¹¹ | 179 | MPa | ASTM D790 |
| Flexural Stress ¹¹ | 181 | MPa | ISO 178 |
| Flexural Modulus ¹¹ | 7510 | MPa | ASTM D790 |
| Flexural Modulus ¹¹ | 7940 | MPa | ISO 178 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 7400 | MPa | ISO 527 |
Table 2 of 5
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.54 | g/cm³ | ASTM D792 |
| Density ¹¹ | 1.54 | g/cm³ | ISO 1183 |
| Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.17 | % | ASTM D570 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.3 | % | ASTM D955 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.33 | % | ISO 294 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.6 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.6 | % | ISO 294 |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.23 | % | ISO 62 |
Table 3 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 203 | °C | ASTM D648 |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 204 | °C | ISO 75/Af |
Table 4 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, at 23°C) ¹¹ | 480 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 69 | J/m | ASTM D256 |
| Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹ | 8 | J | ASTM D3763 |
| Multi-Axial Impact ¹¹ | 2 | J | ISO 6603 |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 32 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 20 | kJ/m² | ISO 180/1A |
Table 5 of 5
12 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 150 | °C |
| Drying Time ⁷ | 4 - 6 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 360 - 375 | °C |
| Rear - Zone 1 Temperature ⁷ | 355 - 365 | °C |
| Middle - Zone 2 Temperature ⁷ | 360 - 370 | °C |
| Front - Zone 3 Temperature ⁷ | 365 - 375 | °C |
| Nozzle Temperature ⁷ | 365 - 375 | °C |
| Mold Temperature ⁷ | 140 - 180 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed (Circumferential speed) ⁷ | 0.2 - 0.3 | m/s |
| Vent Depth ⁷ | 0.025 - 0.076 | mm |