LNP™ LUBRICOMP™ Compound KL004A
LNP LUBRICOMP KL004A compound is based on Acetal (POM) Homopolymer resin containing 20% PTFE. Added features of this grade include: Wear Resistant.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Lawn & Garden
- Consumer Goods — Sports & Recreation
- Consumer Goods — Stationery
- Art & Office Supplies
- Chassis & Brake
- Electrical & Electronic Systems
- Artificial Turf
- Automotive Electronics
- Consumer Electronics
- Displays
- Lighting
- Laboratory & Diagnostics
- Tubing & Fluids Handling
- Non-Food Consumer Packaging
- Applicators & Accessories
- Connectors
- Housings & Enclosures
- Switches & Relays
Product Families
- Polyacetals
Other characteristics
- Brand
- LNP™ LUBRICOMP™ Compound
- Polymer Name
- Polyacetal Homopolymer (POM)
- Fillers Included
- PTFE
- Flexural Modulus
- 2620.0 - 2620.0 MPa
- Additives Included
Anti-Friction Agent, Lubricant (PTFE), Lubricant (Unspecified), Wear Additive; Anti-Friction Agent; Lubricant (PTFE); Lubricant (Unspecified); Wear Additive
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Healthcare & Pharma
- Personal Care
- Printing & Packaging
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Material Features
- Friction Resistant
- Lubricated
- Unreinforced
- Wear Resistant
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Automotive Electronics
- Building Materials
- Cash Dispenser (ATM)
- Cell Phones
- Chassis
- Clinical Diagnostics
- Commercial Appliance
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
19 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 56 | MPa | ASTM D638 |
| Tensile Stress (Break) ¹¹ | 56 | MPa | ASTM D638 |
| Tensile Stress (Break) ¹¹ | 50 | MPa | ISO 527 |
| Tensile Stress (Yield, 5 mm/min) ¹¹ | 46 | MPa | ISO 527 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 11.4 | % | ASTM D638 |
| Tensile Strain (Break) ¹¹ | 11.4 | % | ASTM D638 |
| Tensile Strain (Break) ¹¹ | 9.4 | % | ISO 527 |
| Tensile Strain (Yield, 5 mm/min) ¹¹ | 10 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 2400 | MPa | ISO 527 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 2550 | MPa | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 86 | MPa | ASTM D790 |
| Flexural Stress (Yield, at 2 mm/min) ¹¹ | 74 | MPa | ISO 178 |
Table 2 of 6
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 2 - 2.2 | % | ASTM D955 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 2 - 2.19 | % | ISO 294 |
| Wear Factor Washer ¹¹ | 12 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic COF ¹¹ | 0.23 | — | ASTM D3702 Modified: Manual |
| Static COF ¹¹ | 0.09 | — | ASTM D3702 Modified: Manual |
| Density ¹¹ | 1.52 | g/cm³ | ISO 1183 |
| Density ¹¹ | 1.52 | g/cm³ | ASTM D792 |
| Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.23 | % | ASTM D570 |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.4 | % | ISO 62 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 2 - 2.2 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 2 - 2.19 | % | ISO 294 |
Table 3 of 6
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 157 | °C | ISO 75/Bf |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 98 | °C | ISO 75/Af |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 95 | °C | ASTM D648 |
Table 4 of 6
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 30 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 4 | kJ/m² | ISO 180/1A |
| Izod Impact (Unnotched, at 23°C) ¹¹ | 560 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 42 | J/m | ASTM D256 |
| Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹ | 7 | J | ASTM D3763 |
Table 5 of 6
9 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Melt Temperature ⁷ | 200 - 215 | °C |
| Front - Zone 3 Temperature ⁷ | 210 - 220 | °C |
| Middle - Zone 2 Temperature ⁷ | 195 - 205 | °C |
| Rear - Zone 1 Temperature ⁷ | 175 - 190 | °C |
| Mold Temperature ⁷ | 80 - 110 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |
Table 6 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94HB Flame Class Rating) ᵖ | 1.5 | mm | UL 94 |