LNP™ COLORCOMP™ Compound DX05471-GN8A091

Name: LNP™ COLORCOMP™ Compound DX05471-GN8A091
Brand: LNP™ COLORCOMP™ Compound

LNP COLORCOMP DX05471-GN8A091 compound is based on Polycarbonate (PC) resin. Added features of this grade include: Glow-In-The-Dark.

Product families

Automotive & Transportation — Automotive

Plastics — Engineering & Specialty Polymers

Brand: LNP™ COLORCOMP™ Compound
Polymer Name: Polycarbonate (PC)
Additives Included: Heat Stabilizer
Processing Methods: Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Color: Custom
Markets: Automotive & Transportation
Consumer Goods
Technology: Plastics
Material Features: Excellent Aesthetics
Glow In The Dark
Good Aesthetics
Good Surface Appearance
Heat Stabilized
High Durability
Unreinforced
Plastics and Elastomers End Uses: Automotive Applications
Automotive Interior Parts
Consumer Applications
Home Decoration
Home Decors
Household Goods
Sporting Goods
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

8 rows

Characteristic	Value	Unit	Method
Tensile Stress (Yield, Type I, 50 mm/min) ¹¹	62	MPa	ASTM D638
Tensile Stress (Break, Type I, 50 mm/min) ¹¹	68	MPa	ASTM D638
Tensile Strain (Yield, Type I, 50 mm/min) ¹¹	7	%	ASTM D638
Tensile Strain (Break, Type I, 50 mm/min) ¹¹	130	%	ASTM D638
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹	96	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	2340	MPa	ASTM D790
Hardness (Rockwell M) ¹¹	70	—	ASTM D785
Hardness (Rockwell R) ¹¹	118	—	ASTM D785

6 rows

Characteristic	Value	Unit	Method
Specific Gravity ¹¹	1.2	—	ASTM D792
Water Absorption (at 23°C, 24hrs) ¹¹	0.15	%	ASTM D570
Water Absorption (at 23°C, saturated) ¹¹	0.35	%	ASTM D570
Water Absorption (Equilibrium, at 100°C) ¹¹	0.58	%	ASTM D570
Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹	0.5 - 0.7	%	SABIC method
Melt Flow Rate (at 300°C, 1.2 kgf) ¹¹	10.5	g/10 min	ASTM D1238

3 rows

Characteristic	Value	Unit	Method
Heat Deflection Temperature (at 0.45 MPa, 6.4 mm, Unannealed) ¹¹	137	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹	132	°C	ASTM D648
Coefficient of Thermal Expansion (at -40°C to 95°C, flow) ¹¹	0.0000684	1/°C	ASTM E831

3 rows

Characteristic	Value	Unit	Method
Izod Impact (Unnotched, at 23°C) ¹¹	3204	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	801	J/m	ASTM D256
Tensile Impact Strength (Type S) ¹¹	577	kJ/m²	ASTM D1822

14 rows