LNP™ COLORCOMP™ Compound D1000P

Chemical Family: Polycarbonate (PC)

SABIC's Specialties Business LNP COLORCOMP D1000P compound is based on unfilled Polycarbonate (PC) resin. Added features of this grade include: Exceptional Processing. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.

Product families

Applications

Consumer Goods — Appliances & Electronics
Consumer Goods — Housewares
Consumer Goods — Sports & Recreation

Automotive & Transportation — Automotive

Interior

Electrical & Electronics — Devices & Assemblies

Consumer Electronics
Displays

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics
Polycarbonates

Other characteristics

Brand: LNP™ COLORCOMP™ Compound
Polymer Name: Polycarbonate (PC)
Flexural Modulus: 2750.0 - 2750.0 MPa
Additives Included: Mold Release Agent
Processing Methods: Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Color: Custom
Markets: Automotive & Transportation
Consumer Goods
Electrical & Electronics
Personal Care
Printing & Packaging
Technology: Plastics
Labeling Claims: No Added PFAS
Material Features: Excellent Aesthetics
Good Aesthetics
Good Mold Release
Good Processability
Good Surface Appearance
High Durability
High Flowability
No Added PFAS
Plastics and Elastomers End Uses: Appliances
Automotive Applications
Automotive Interior Parts
Cell Phones
Commercial Appliance
Computer Components
Consumer Applications
Containers
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 5

13 rows

Characteristic	Value	Unit	Method
Tensile Stress (Yield) ¹¹	62	MPa	ASTM D638
Tensile Stress (Yield) ¹¹	64	MPa	ISO 527
Tensile Stress (Break) ¹¹	56	MPa	ASTM D638
Tensile Stress (Break) ¹¹	59	MPa	ISO 527
Tensile Strain (Yield) ¹¹	5.3	%	ASTM D638
Tensile Strain (Yield) ¹¹	5.6	%	ISO 527
Tensile Strain (Break) ¹¹	78.7	%	ASTM D638
Tensile Strain (Break) ¹¹	87	%	ISO 527
Tensile Modulus (at 50 mm/min) ¹¹	2060	MPa	ASTM D638
Flexural Modulus ¹¹	2750	MPa	ASTM D790
Flexural Modulus ¹¹	2300	MPa	ISO 178
Tensile Modulus (at 1 mm/min) ¹¹	2210	MPa	ISO 527

Table 2 of 5

7 rows

Characteristic	Value	Unit	Method
Density ¹¹	1.2	g/cm³	ASTM D792
Density ¹¹	1.19E+00	g/cm³	ISO 1183
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.6 - 0.8	%	ASTM D955
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.65	%	ISO 294
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	0.7 - 0.9	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	0.75	%	ISO 294
Melt Flow Rate (at 300°C, 1.2 kgf) ¹¹	24	g/10 min	ASTM D1238

Table 3 of 5

2 rows

Characteristic	Value	Unit	Method
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	123	°C	ASTM D648
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	124	°C	ISO 75/Af

Table 4 of 5