LNP™ COLORCOMP™ Compound D1000RFU
- Chemical Family
- Polycarbonate (PC)
LNP COLORCOMP D1000RFU compound is based on Polycarbonate (PC) resin. Added features of this grade include: Mold Release, UV Stabilized, Superior Molding.
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Sports & Recreation
Automotive & Transportation — Automotive
- Interior
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
- Displays
Printing & Packaging — Packaging
- Non-Food Consumer Packaging
Personal Care — Packaging & Accessories
- Applicators & Accessories
Electrical & Electronics — Parts & Components
- Connectors
- Switches & Relays
Product Families
Plastics — Engineering & Specialty Polymers
- High Performance Thermoplastics
- Polycarbonates
Other characteristics
- Brand
- LNP™ COLORCOMP™ Compound
- Polymer Name
- Polycarbonate (PC)
- Additives Included
- Mold Release Agent, UV Stabilizer
- Mold Release Agent
- UV Stabilizer
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Color
- Custom
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Material Features
- Excellent Aesthetics
- Good Aesthetics
- Good Mold Release
- Good Moldability
- Good Surface Appearance
- Good UV Stability
- Good Weather Stability
- High Flowability
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Interior Parts
- Cell Phones
- Computer Components
- Consumer Applications
- Containers
- Displays
- Electrical Components
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 8
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 62 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 65 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ | 7 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 110 | % | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 93 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2340 | MPa | ASTM D790 |
| Hardness (Rockwell M) ¹¹ | 70 | — | ASTM D785 |
| Hardness (Rockwell R) ¹¹ | 118 | — | ASTM D785 |
| Taber Abrasion (CS-17, 1 kg) ¹¹ | 10 | mg/1000cy | ASTM D1044 |
Table 2 of 8
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.2 | — | ASTM D792 |
| Specific Volume ¹¹ | 0.83 | cm³/g | ASTM D792 |
| Density ¹¹ | 1.19 | g/cm³ | ASTM D792 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.15 | % | ASTM D570 |
| Water Absorption (at 23°C, saturated) ¹¹ | 0.35 | % | ASTM D570 |
| Water Absorption (Equilibrium, at 100°C) ¹¹ | 0.58 | % | ASTM D570 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.5 - 0.7 | % | SABIC method |
| Melt Flow Rate (at 300°C, 1.2 kgf) ¹¹ | 17.5 | g/10 min | ASTM D1238 |
Table 3 of 8
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat Softening Temperature (Rate B/50) ¹¹ | 154 | °C | ASTM D1525 |
| Heat Deflection Temperature (at 0.45 MPa, 6.4 mm, Unannealed) ¹¹ | 137 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 132 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 95°C, flow) ¹¹ | 0.0000684 | 1/°C | ASTM E831 |
| Specific Heat ¹¹ | 1.26 | J/g-°C | ASTM C351 |
| Thermal Conductivity ¹¹ | 0.19 | W/m-°C | ASTM C177 |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 130 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 130 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 130 | °C | UL 746B |
Table 4 of 8
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volume Resistivity ¹¹ | 1.00E+17 | Ω.cm | ASTM D257 |
| Dielectric Strength (in air, at 3.2mm) ¹¹ | 15 | kV/mm | ASTM D149 |
| Relative Permittivity (50/60 Hz) ¹¹ | 3.17 | — | ASTM D150 |
| Relative Permittivity (1 MHz) ¹¹ | 2.96 | — | ASTM D150 |
| Dissipation Factor (at 50/60 Hz) ¹¹ | 0.0009 | — | ASTM D150 |
| Dissipation Factor (at at 1 MHz) ¹¹ | 0.01 | — | ASTM D150 |
| High Voltage Arc Track Rate (PLC) ¹¹ | 2 | PLC Code | UL 746A |
| Comparative Tracking Index (UL, PLC) ¹¹ | 2 | PLC Code | UL 746A |
| Hot Wire Ignition (PLC 4) ¹¹ | min. 1.5 | mm | UL 746A |
| High Ampere Arc Ignition (PLC 1) ¹¹ | min. 3 | mm | UL 746A |
| High Ampere Arc Ignition (PLC 2) ¹¹ | min. 1.5 | mm | UL 746A |
Table 5 of 8
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Light Transmission (at 2.54 mm) ¹¹ | 88 | % | ASTM D1003 |
| Haze (at 2.54 mm) ¹¹ | 1 | % | ASTM D1003 |
| Refractive Index ¹¹ | 1.586 | — | ASTM D542 |
Table 6 of 8
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, at 23°C) ¹¹ | 3204 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 694 | J/m | ASTM D256 |
| Tensile Impact Strength (Type S) ¹¹ | 546 | kJ/m² | ASTM D1822 |
| Falling Dart Impact (at 23°C) ¹¹ | 169 | J | ASTM D3029 |
Table 7 of 8
14 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 120 | °C |
| Drying Time ⁷ | 3 - 4 | Hrs |
| Drying Time (Cumulative) ⁷ | 48 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 280 - 305 | °C |
| Nozzle Temperature ⁷ | 275 - 300 | °C |
| Front - Zone 3 Temperature ⁷ | 280 - 305 | °C |
| Middle - Zone 2 Temperature ⁷ | 270 - 295 | °C |
| Rear - Zone 1 Temperature ⁷ | 260 - 280 | °C |
| Mold Temperature ⁷ | 70 - 95 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed ⁷ | 40 - 70 | rpm |
Table 8 of 8
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94HB Flame Class Rating) ᵖ | min. 0.75 | mm | UL 94 |
| UV-light (Water exposure/immersion) ᵖ | F1 | — | UL 746C |