Nizhnekamskneftekhim High-Impact Polystyrene 825Е
- Chemical Family
- High-Impact Polystyrene (HIPS)Styrenics
Nizhnekamskneftekhim High-Impact Polystyrene 825Е is an high impact polystyrene is produced by bulk block copolymerization of styrene and butadiene rubber. It is used for manufacture of industrial packaging by thermoforming and for extrusion molding of multilayer profile sheets. It is used for thin wall extrusion.
Properties
- Physical Form
- Pellets
- Solid
Product families
Applications
Applications
- Electrical & Electronics — Other Electrical & Electronics Applications; Printing & Packaging — Other Printing & Packaging Applications
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Electrical & Electronics — Devices & Assemblies
- Other Devices & Assemblies
Printing & Packaging — Packaging
- Industrial & Transport Packaging
Electrical & Electronics — Packaging & Assembly
- Other Packaging & Assembly Applications
Adhesives & Sealants — Packaging & Paper
- Other Packaging & Paper Applications
Electrical & Electronics — Parts & Components
- Other Parts & Components
Product Families
Plastics — Basic Thermoplastics
- Styrenics
Other characteristics
- Polymer Name
- High Impact Polystyrene (HIPS)
- Melt Flow Index
- 2.0 - 4.0 g/10 min
- Processing Methods
- Thermoforming
- Markets
- Adhesives & Sealants
- Electrical & Electronics
- Industrial
- Printing & Packaging
- Storage
In closed room on shelves or pallets, at a distance of minimum 5 cm above the floor and at a distance of minimum 1 m from the space heaters, in conditions, excluding direct sunlight effect.
- PACKAGING
- Polyethylene bags, in bulk by polymer trucks.
- Technology
- Plastics
- Packaging Type
- Bags
- Plastics and Elastomers End Uses
- Industrial Applications
- Thermoforming Applications
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Thermoforming
Technical data
Table 1 of 1
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt flow rate at 200°С per 5 kg of Load | 3.0±1.0 | g/10min | ASTM D 1238 |
| Vicat softening temperature | min.92 | °С | ASTM D 1525 |
| Tensile strength | min.21 | MPa | ASTM D638 |
| Elongation at Break | min.45 | % | ASTM D638 |
| Izod Impact Strength, Notched | min.96 | J/m | ISO 180 |
| Flexural Strength | min.41 | MPa | ASTM D790 |
| Gloss at 60° | min.50 | — | ASTM D523 |
| Residual Styrene Mass Fraction | max. 0.05 | wt% | para. 4.10 TU |